Compatibilized Thermoplastic Vulcanizate Compositions

ABSTRACT

This invention relates to a thermoplastic vulcanizate having excellent elongation comprising an isotactic polypropylene matrix phase in which a cross-linked ethylene-propylene-diene terpolymer (EPDM) is dispersed, the vulcanizate comprising the reaction product of:
     a) 35 to 55 wt % of an ethylene-propylene-diene terpolymer (EPDM);   b) 10 to 40 wt % of isotactic polypropylene (iPP);   c) 0.5 to 25 wt % of a propylene-ethylene-diene terpolymer (PEDM) compatibilizer, said compatibilizer having a heat of fusion of less than 2 J/g; and   d) 0.015 to 0.03 wt % of curatives;   wherein the percentages of components (a) to (d) are based on the total weight of the mixture.

PRIORITY CLAIM

This application claims priority to and the benefit of U.S. Ser. No. 62/653,734 filed Apr. 6, 2018 and is incorporated by reference in its entirety.

STATEMENT OF RELATED APPLICATIONS

This invention also relates to:

1) U.S. Ser. No. ______, filed concurrently herewith, entitled “Thermoplastic Vulcanizate Compositions”, attorney docket number (2019EM076);

2) U.S. Ser. No. ______, filed concurrently herewith, entitled “Thermoplastic Vulcanizates and Compositions Therefrom”, attorney docket number (2019EM081);

3) U.S. Ser. No. ______, filed concurrently herewith, entitled “Processes for Producing High Propylene Content PEDM using Tetrahydroindacenyl Catalyst Systems”, attorney docket number (2018EM053/2), which claims priority to and the benefit of U.S. Ser. No. 62/644,971, filed Mar. 19, 2018;

4) U.S. Ser. No. ______, filed concurrently herewith, entitled “Processes for Producing High Propylene Content PEDM Having Low Glass Transition Temperatures Using Tetrahydroindacenyl Catalyst Systems”, attorney docket number (2018EM053A); which claims priority to and the benefit of U.S. Ser. No. 62/644,971, filed Mar. 19, 2018;

5) U.S. Ser. No. ______, filed concurrently herewith, entitled “Multiple Non-Coordinating Anion Activators for Propylene-Ethylene-Diene Monomer Polymerization Reactions”, attorney docket number (2019EM070); and

6) U.S. Ser. No. ______, filed concurrently herewith, entitled “Compatibilized Thermoplastic Vulcanizate Compositions”, attorney docket number (2018EM063/2) claims priority to and the benefit of U.S. Ser. No. 62/653,734 filed Apr. 6, 2018.

FIELD

The present disclosure relates to thermoplastic vulcanizate compositions and methods for preparing them.

BACKGROUND

The first commercial thermoplastic vulcanizate, or TPV, was Santoprene™, which was introduced early in the 1980s. Thermoplastic vulcanizates are thermoplastic elastomers, not thermoset rubbers, and can be processed or re-processed as thermoplastics. Thermoplastic vulcanizates differ from thermoplastics at least by inclusion of dispersed vulcanized rubber particles. Vulcanization, or crosslinking, of rubbers in TPVs is necessary to keep the rubber, which is the majority blend component, as the dispersed phase, instead of the continuous phase. Following the Paul-Barrow continuity criterion (D. R. Paul and J. W. Barlow, J. Maromol. Sci., Rev. Macromol. Chem., C18, 109, (1980)), where phi 1/phi 2=eta 1/eta 2, the phase with infinite viscosity, such as crosslinked rubbers, would stay dispersed. This allows the packing of a maximum amount of rubber dispersion in a plastic matrix without rubber phase inversion. The maximum packing volume percent is limited by packing physics and is typically less than 70 vol %. By squeezing in greater than 60 vol % of crosslinked rubber dispersions inside a plastic matrix, the plastic matrix becomes inter-connecting plastic ligaments sandwiched in between dispersed crosslinked rubber particles.

Without being bound by any theory, the elasticity of a TPV is thought to derive from these thin plastic ligaments sandwiched between dispersed rubber particles. Based on experimental findings and theoretic modeling (e.g., as by M. C. Boyce, S. Socrate, K. Kear, O. Yeh, and K. Shaw, J. Mech. Phys. Solids, 49, 1323, (2001), and J. Mech. Phys. Solids, 49, 1343, (2001), these thin plastic ligaments kink or plastic flow during TPV deformation by the incompressible deformation of sandwiching crosslinked rubber dispersions. Subsequently, these plastic ligament kinks act as spatial registrations to allow elastic recovery and to deliver elasticity. Thinner plastic ligaments would be easily deformed and also yield easily, for plastic flow/kink formation, relative to thick plastic ligaments. If the plastic matrix has plastic patches that are relatively large between dispersed rubber particles, these plastic flows and kink developments are not possible and this leads to poorer elastic properties. Rubber dispersion size and uniformity are important to create a uniform plastic ligament network. Greater uniformity of the plastic ligament network promotes the elastic properties of a TPV.

The particle size and uniformity of the rubber dispersion in a TPV thus can constrain the selection of plastic and rubber components for the preparation of a TPV. For a Santoprene™ TPV, which is a TPV based on isotactic polypropylene (iPP) plastic matrix, and crosslinked ethylene-propylene-diene terpolymer (EPDM) rubber dispersions, it is important to use fractional melt-flow rate (MFR) iPP to blend with EPDM in a mixer before the introduction of curatives. Since EPDM typically has much higher molecular weight (MW) than that of an iPP, use of low MFR and high MW iPP provides helpful viscosity matching during initial blending. Viscosity matching allows stress transfer across blend interfaces to produce finer dispersions (L. A. Utracki, “Polymer Alloys and Blends—Thermodynamics and Rheology”, Hanser Publishers, New York, (1990)). In the case of preparing TPVs, viscosity matching promotes fine iPP dispersions inside the EPDM matrix. Once the curatives are introduced, phase inversion occurs and crosslinked EPDM becomes the dispersed phase. Although decent dispersion of crosslinked rubber can be obtained in a TPV by judicious selections of plastic and rubber components (for viscosity matching) and of twin screw extrusion elements (for phase inversion and rubber dispersion in the production process), crosslinked rubber dispersion uniformity in a TPV can be further improved for better elastic properties.

Additionally it is thought that compatibilizers in polymer blends can suppress droplet coalescence, reduce interfacial tension, and lead to finer dispersions (L. A. Utracki, “Polymer Alloys and Blends—Thermodynamics and Rheology”, Hanser Publishers, New York, (1990)).

SUMMARY

In the present disclosure, a crosslinkable thermoset rubber compatibilizer, comprising (or consisting of, or consisting essentially of) one or more propylene-ethylene-diene terpolymer(s) (PEDM), is added to compatibilize blends of EPDM and iPP prior to phase inversion during dynamic vulcanization. The compatibilizer can be synthesized by organometallic coordinative insertion polymerization of propylene, ethylene, and diene—with majority propylene, preferably greater than 80 wt % by weight of the PEDM terpolymer. Using PEDM compatibilizers in polymer blends can suppress droplet coalescence, reduce interfacial tension, and lead to finer dispersions. Adding a PEDM compatibilizer during PP/EPDM TPV preparation prior to vulcanization can provide fine PP dispersions, which, after vulcanization and phase inversion, provide fine dispersions of vulcanized EPDM inside the TPV with a result of improved mechanical toughness.

Accordingly, disclosed herein is a thermoplastic vulcanizate comprising an isotactic polypropylene matrix phase in which a cross-linked ethylene-propylene-diene terpolymer (EPDM) is dispersed, the vulcanizate being a reaction product of a mixture of:

a) 35 to 55 wt % of an ethylene-propylene-diene terpolymer (EPDM);

b) 10 to 40 wt % of isotactic polypropylene (iPP);

c) 0.5 to 25 wt % of a propylene-ethylene-diene terpolymer (PEDM) compatibilizer (preferably having a heat of fusion (Hf) of less than 2 J/g, preferably less than 1 j/g, preferably having no detectable Hf); and

d) At least 0.015 (typically 0.015 to 0.03) wt % of curatives;

wherein the percentages of components (a), (b), (c) and (d) are based on the total weight of the mixture.

For purposes of this invention and the claims thereto, a heat of fusion of less than 2 J/g includes a heat of fusion that is undetectable.

In some embodiments, the thermoplastic vulcanizate further comprises at least 10 wt % of a diluent.

In some embodiments, the EPDM comprises 55 to 75 wt % ethylene, 2 to 10 wt % 5-ethylidene-2-norbornene, with the balance being propylene, preferably the EPDM comprises 55 to 75 wt % ethylene, 2 to 10 wt % 5-ethylidene-2-norbornene, and 43 to 15 wt % propylene.

In some embodiments, the amount of PEDM in the TPV is present at from 2 to 30 wt % of the amount of EPDM.

In some embodiments, the PEDM has viscosity of MST (5+4) @230 C is from 5 to 90.

In some embodiments, the PEDM comprises 5 to 18 wt % ethylene and 2 to 12 wt % 5-ethylidene-2-norbornene with the balance being propylene.

In some embodiments, the particle size dispersity index (PSDI) of the rubber particles is less than 3.

In some embodiments, the thermoplastic vulcanizate further comprises clay and carbon black.

In some embodiments, the PEDM has a heat of fusion (Hf) which is greater than or equal to 0 and less than 2 J/g.

In some embodiments, the PEDM has a heat of fusion (Hf) which is greater than or equal to 0 and less than or equal to 1 J/g.

The present disclosure also encompasses a TPV composition made by such a method comprising (or consisting of, or consisting essentially of):

i) mixing an iPP, EPDM, and PEDM, and a diluent to prepare a TPV formulation;

ii) adding one or more curatives to the TPV formulation and continuing mixing to perform dynamic vulcanization; and

iii) recovering the TPV composition.

In some embodiments, the method further comprises adding a diluent to the TPV formulation prior to step ii) and continuing mixing.

In some embodiments, the method further comprises adding a further portion of diluent following step ii) and continuing mixing and dynamic vulcanization to form a TPV composition.

In some embodiments, the curatives are a resin in oil (RIO) composition (typically a phenolic resin in oil), stannous chloride and zinc oxide.

In some embodiments, the ethylene-propylene-diene terpolymer (EPDM) is added in an amount from 35-55 wt % of the TPV formulation, the isotactic polypropylene (iPP) is added in an amount from 10 to 40 wt % of the TPV formulation; diluent is added in an amount from 13 to 21 wt % of the TPV formulation, and a propylene-ethylene-diene terpolymer (PEDM) compatibilizer is added in an amount from 0.5-15 wt % of the TPV formulation.

In some embodiments, the method is performed at a temperature of from 150 to 200° C. in an internal mixer running at from 80 to 120 rpm and mixing continues for about 1 minute prior to step ii), for about 2 minutes after the first addition of diluent, for about 5 minutes after the second addition of diluent and for about 3 minutes after step iii).

In some embodiments, the method is performed at a temperature from 200 to 250° C. in a continuous twin-screw extruder running at from 50 to 200 RPM with 1 to 5 minutes of residence time wherein the iPP, EPDM, and PEDM, and first portion of a diluent are added to the extruder at a first position of the extruder, and at least one of the second portion of diluent, the curatives and the third portion of diluent are added to the extruder at least a second position downstream from the first position.

In some embodiments, the method is performed at a temperature of from 150 to 200° C. in an internal mixer running at from 80 to 120 rpm and mixing continues for about 1 minute after step i), for about 2 minutes after the first addition of diluent, for about 5 minutes after the second addition of diluent and for about 3 minutes after step iii); and then mixing is performed for about 1 to 5 additional minutes.

In some embodiments, the method is performed at a temperature from 200 to 250° C. in a continuous twin-screw extruder running at from 50 to 200 RPM with 1 to 5 minutes of residence time; and in which a curative agent is added as a resin in oil composition is added to the extruder at a first position, followed by additional mixing.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1A illustrates rubber dispersion size and plastic ligament formation (left: large dispersions (only 2 ligaments), right: small dispersions (16 ligaments), both have the same rubber volume percent).

FIG. 1B illustrates rubber dispersion uniformity and plastic ligament formation (left: poor dispersion uniformity, right: good dispersion uniformity, both have the same rubber volume percent).

FIG. 2 illustrates schematically one embodiment of a process as disclosed herein and an associated apparatus.

FIG. 3 shows a graph of the correlation of elastic recovery to particle size dispersion in EPDM/iPP TPV.

FIGS. 4A-4G show EPDM rubber dispersions in TPV compositions: 4A—0 wt % of PEDM2; 4B—2 wt % of PEDM2; 4C—5 wt % of PEDM2; 4D -10 wt % of PEDM2; 4E—15% of PEDM2; 4F—20 wt % of PEDM2 and 4G—30 wt % of PEDM2, as described in U.S. Ser. No. ______, filed concurrently herewith, entitled “Compatibilized Thermoplastic Vulcanizate Compositions”, attorney docket number (2018EM063/2) claims priority to and the benefit of U.S. Ser. No. 62/653,734 filed Apr. 6, 2018.

FIGS. 5A-5C show EPDM rubber dispersions in example TPV compositions with V3666 as the EPDM: 5A contains 5 wt % PEDM (having 16 wt % ethylene); 5B contains 15 wt % PEDM (having 16 wt % ethylene); 5C contains 25 wt % PEDM (having 16 wt % ethylene).

FIGS. 6A-6B show tension set for 25% and 50% elongation for inventive samples.

FIGS. 7A-7B show diameter of the rubber particles and the dispersity in the particle size for inventive samples.

FIGS. 8A-8B show tensile strength and the elongation of the TPV for inventive samples.

DETAILED DESCRIPTION

In the present disclosure, a crosslinkable thermoset rubber compatibilizer is added to compatibilize blends of EPDM and iPP prior to their phase inversion by vulcanization. Such a compatibilizer is typically synthesized by organometallic coordinative insertion polymerization of propylene, ethylene and diene, with majority (generally greater than 60, typically greater than 80 wt %) propylene, and is called a propylene-ethylene-diene terpolymer (PEDM). Utilizing PEDM compatibilizers in polymer blends can suppress droplet coalescence, reduce interfacial tension, and lead to finer. Adding a PEDM compatibilizer during PP/EPDM TPV preparation prior to vulcanization can provide fine PP dispersions, which, after vulcanization and phase inversion, lead to fine EPDM dispersions inside the TPV, which provides a TPV with improved mechanical toughness. FIG. 1A shows that the number of plastic ligaments in a network increases with decreasing size of the rubber particles dispersed in the plastic matrix phase. FIG. 1B shows how increasing the uniformity of the rubber particle size dispersion provides a more distributed and more uniform plastic filament network having thinner ligaments.

For example, a TPV composition as presently disclosed can be one that has a particle size dispersity index (PSDI) of less than 5.0, although more typically the PSDI in a TPV composition as presently disclosed is less than 4.0, or less than 3.5, or less than 3.0. For example, the PSDI of a TPV according to the present disclosure can be from 1.2-6.5, or from 1.2-5, from 1.2-4, from 1.2-3.5, from 1.2-3.0, or from 1.5-3.0.

In embodiments of the invention, the amount of PEDM in the TPV is present at 2 to 30 wt % of the amount of EPDM, preferably from 2 wt %, 5 wt %, 10 wt %, 15 wt %, 20 wt % or 25 wt % to 30 wt % of the amount of EPDM, alternately from 5 wt % to 25 wt %, alternately from 10 to 20 wt %. In embodiments of the invention, the ratio of PEDM in the TPV to EPDM in the TPV is less than 1:1, preferably less than 1:3.3, preferably less than 1:5, preferably from 0.05:1 to 1:3.

TPV Compositions

Thermoplastic vulcanizate (TPV) compositions of various embodiments may comprise, consist essentially of, or consist of: (a) an at least partially vulcanized rubber component dispersed within a continuous thermoplastic matrix; (b) oil; and, optionally, (c) one or more additives (e.g., one or more fillers, foaming agents, compatibilizers or the like). As used in this context, “consist essentially of” means that the TPV composition is free of other materials except those minor impurities (e.g., 0.1 wt % or less) that one would typically expect in normal commercial production operations. For instance, a single process line may be used in a continuous process to create multiple different types of materials in series, and some residuals (e.g., residual polymer, monomer, curative, additives, or other material) from previous product campaigns may acceptably be left in such equipment and thus incorporated into a TPV product.

Composition TPVs are formed by dynamically vulcanizing a TPV formulation. The TPV formulation of various embodiments comprises (i) a rubber component (which may or may not be oil-extended); (ii) a thermoplastic resin; (iii) an optional, polyolefin-based, typically propylene-based, elastomer (PBE) (which may be especially useful in compositions comprising Santoprene™) or a hydrogenated triblock copolymerized thermoplastic elastomer (TPE—for example hydrogenated Kraton™ (Kraton Polymers)); (iv) a vulcanizing agent or curative; (v) processing oil; (vi) a compatibilizer; and (vii) optionally, one or more additives (including, e.g., cure accelerators, metal oxides, acid scavengers, flame retardants, fillers, stabilizers, and the like). A TPV product may therefore alternatively be considered and described as the reaction product of dynamic vulcanization of a TPV formulation or “melt”, or as a “dynamically vulcanized alloy” (DVA).

A TPV composition can be prepared in which the rubber component is not vulcanized, but instead comprises polymer chains associated with one another by physical means and thus promoting the inversion of the rubber and plastic phases, such as hydrogen bonds, ionic aggregation, and phase transition (e.g., crystallization or a glass transition); thus, a TPV formulation not yet subjected to a covalent cross-linking chemical reaction can be prepared in which physical cross links can be removed by heating.

In embodiments of the invention herein, the TPV has an elongation at break of 200% or more, alternately 225% or more, alternately 250% or more, as determined by the method described below.

In embodiments of the invention herein, the TPV has a break stress of 4 MPa or more, alternately 5 MPa or more, as determined by the method described below.

In embodiments of the invention herein, the TPV has a tension set from 25% elongation of 7% or less, alternately 6% or less, alternately 5% or less, as determined by the method described below.

In embodiments of the invention herein, the TPV has a tension set from 50% elongation of 14% or less, alternately 12% or less, alternately 10% or less, as determined by the method described below.

In embodiments of the invention herein, the TPV has an number average particle size diameter of the rubber particles of 800 nm or less, alternately 700 nm or less, alternately 600 nm or less, as determined by the method described below.

In embodiments of the invention herein, the TPV has a dispersity of crosslinked particle size diameter of the rubber particles of 1.6 or less, alternately 1.5 or less, alternately 1.4 or less, or 1.3 or less as determined by the method described below.

Rubber Component

The “rubber” component of TPV formulations or compositions generally is a crosslinkable (vulcanizable) rubber component, such that upon dynamic vulcanization, the rubber component in the resulting TPV composition (i.e., resulting from processing, including by dynamic vulcanization, of the TPV formulation) of such embodiments is at least partially crosslinked, preferably fully crosslinked. Generally, the term “rubber” refers to any natural or synthetic polymer exhibiting elastomeric properties, and may be used herein synonymously with “elastomer.” The rubber component may comprise one rubber, or a mix of two or more rubbers.

In the TPV compositions presently disclosed, one or more EPDM rubbers are used as the rubber component.

For example, the rubber component can be any ethylene-propylene-diene (EPDM) rubber, or EPDM-type rubber, for example, an EPDM-type rubber can be a terpolymer derived from the polymerization of at least two different monoolefin monomers having from 2 to 10 carbon atoms, preferably 2 to 4 carbon atoms, and at least one poly-unsaturated olefin having from 5 to 20 carbon atoms. U.S. Pat. Nos. 3,037,954 and 4,811,628, hereby incorporated by reference in their entirety and for all purposes, describe TPVs having a polypropylene matrix and EPDM rubber component.

The EPDM rubber can be one that comprises from 50-80 wt % ethylene and 1-15 wt % ethylene norbornene, based on the weight of the EPDM rubber, with the balance being propylene. More typically, the EPDM rubber can be one that comprises from 45-75 wt % ethylene and 2-10 wt % ethylene norbornene, or from 50-65% ethylene and 2 to 10% ethylene norbornene, with the balance being propylene.

The EPDM rubber can be one that comprises at least 40 wt %, such from 50-80 wt %, of ethylene-derived units and 1-15 wt % of diene-derived units. Dienes may be conjugated or non-conjugated, acyclic or cyclic. Preferably, the dienes are non-conjugated. Dienes can include 5-ethylidene-2-norbornene (ENB); 5-vinyl-2-norbornene (VNB); 1,4-hexadiene; 5-methylene-2-norbornene (MNB); 1,6-octadiene; 5-methyl-1,4-hexadiene; 3,7-dimethyl-1,6-octadiene (MOD); 1,3-cyclopentadiene; 1,4-cyclohexadiene; dicyclopentadiene (DCPD); and combinations thereof. Other exemplary dienes include butadiene, pentadiene, hexadiene, heptadiene, octadiene, nonadiene, decadiene, undecadiene, dodecadiene, tridecadiene, tetradecadiene, pentadecadiene, hexadecadiene, heptadecadiene, octadecadiene, nonadecadiene, icosadiene, heneicosadiene, docosadiene, tricosadiene, tetracosadiene, pentacosadiene, hexacosadiene, heptacosadiene, octacosadiene, nonacosadiene, triacontadiene, and isomers thereof. Examples of α,ω-dienes include 1,6-heptadiene, 1,7-octadiene, 1,8-nonadiene, 1,9-decadiene, 1,10-undecadiene, 1,11-dodecadiene, 1,12-tridecadiene, 1,13-tetradecadiene. Low molecular weight polybutadienes (Mw less than 1000 g/mol) may also be used as the diene, which is sometimes also referred to as a polyene. Suitable dienes comprise 5-ethylidene-2-norbornene (ENB), 5-vinyl-2-norbornene, divinyl benzene, and dicyclopentadiene, with ENB being preferred. More typically, the EPDM rubber can be one that comprises from 45-75 wt % ethylene and 2-10 wt % ethylene norbornene, or from 50-65% ethylene and 2 to 10% ethylene norbornene.

The rubber component is preferably present in the TPV formulation in an amount within the range from 40 to 80 wt %, preferably 50 to 70 wt %, such as 55 to 65 wt %, based on total weight of the TPV, excluding both of processing and extender oils, with ranges from any of the foregoing low ends to any of the foregoing high ends also contemplated in various embodiments. Note that these wt % values for rubber component are exclusive of any extender oil that may be formulated with the rubber component (e.g., for ease of processing). The TPV formulation of some embodiments may optionally comprise 5 to 30 wt %, such as 10 to 25 wt % or 12 to 24 wt % (with ranges from any of the foregoing lows to any of the foregoing highs also contemplated) of extender oil, where the rubber component includes extender oil.

Alternatively, the rubber component amount in the TPV composition may be expressed in terms of wt % inclusive of any extender oil that may be present in the rubber component, but not including any oil added during processing (“processing oil”). In such cases, the rubber component (inclusive of extender oil) may be present in the TPV composition within the range from 35 to 80 wt %, preferably 45 to 70 wt %, such as 50 to 65 wt % (again, with ranges from any of the foregoing lows to any of the foregoing highs also contemplated in various embodiments).

Thermoplastic Component

TPV formulations and/or TPV compositions generally include a thermoplastic component comprising at least one olefinic thermoplastic resin. The thermoplastic resin may be a polymer or polymer blend considered by persons skilled in the art as being thermoplastic in nature, e.g., a solid polymer that softens and becomes molten when exposed to heat and returns to solid when cooled to 23° C. The olefinic thermoplastic component may contain one or more polyolefins, including polyolefin homopolymers and polyolefin copolymers.

The term “polypropylene” as used herein broadly means any polymer that is considered a “polypropylene” by persons skilled in the art and includes homopolymers as well as impact, random, and other copolymers of propylene. Preferably, the polypropylene used in the TPVs described herein has a melting point above 110° C. and includes at least 90 wt % propylene-derived units. The polypropylene may also include isotactic, atactic or syndiotactic sequences, and preferably includes isotactic sequences. The polypropylene can either derive exclusively from propylene monomers (i.e., having only propylene-derived units) or comprises at least 90 wt %, or at least 93 wt %, or at least 95 wt %, or at least 97 wt %, or at least 98 wt %, or at least 99 wt % propylene-derived units, with the remainder derived from one or more olefins selected from the group consisting of ethylene and C₄ to C₁₀ α-olefins.

The thermoplastic resin (preferably iPP) may have a melting temperature of at least 110° C. (230° F.), or at least 120° C. (248° F.), or at least 130° C. (266° F.), and may range from 110° C. (230° F.) to 170° C. (338° F.) or higher as measured by Differential Scanning Calorimetry (DSC) as described in detail below.

The procedure for DSC analysis of thermoplastic is as follows: 6 to 10 mg of a sheet of the sample pressed at approximated 200° C. (392° F.) to 230° C. (446° F.) is removed with a punch die and then annealed at about 23° C. (74° F.) for 240 hours. At the end of this period, the sample is placed in a Differential Scanning Calorimeter (Perkin Elmer 7 Series Thermal Analysis System) and cooled at a rate of 10° C. (50° F.)/min to −50° C. (−58° F.) to −70° C. (−274° F.). The sample is then heated at a rate of 20° C. (68° F.)/min to attain a final temperature of 200° C. (392° F.) to 220° C. (428° F.). The thermal output during this heating cycle is recorded as the area under the melting peak of the sample and is measured in Joules as a measure of the heat of fusion. The melting temperature is recorded as the temperature of the greatest heat absorption within the range of melting of the sample.

In some embodiments, the thermoplastic resin (preferably iPP) has MFR of 20 g/10 min or less, 15 g/10 min or less, more preferably 10 or less, 5 or less, 3 or less, or even 1 or less, in some embodiments (measured per ASTM D1238, at 230° C. (446° F.) and 2.16 kg mass). For instance, MFR of the thermoplastic resin may be within the range from a low of any one of 0.01, 0.1, and 0.5 g/10 min to a high of any one of 1, 3, 5, 10, 15, 16 or 20 g/10 min (ASTM D1238, 230° C. (446° F.) and 2.16 kg). In certain of these embodiments, the thermoplastic component comprises only thermoplastic resin with MFR according to the foregoing description.

In yet other embodiments the TPV composition (and/or the TPV formulation) may comprise two or more thermoplastic resins, which can be two or more polypropylene resins. In particular, the TPV composition may comprise (i) a low-MFR thermoplastic resin having MFR of 15 g/10 min or less (or other MFR per the above description); and (ii) a high-MFR thermoplastic resin having MFR of greater than 15 g/10 min, for instance, within the range from greater than 15 to 50 g/10 min, preferably within the range from greater than 15 to 25 g/10 min, such as 16 to 24 g/10 min. The high-MFR thermoplastic resin may otherwise be in accordance with the above-given descriptions of suitable thermoplastic resins (e.g., with respect to monomeric constituents, melting temperature, and the like). In certain of these embodiments employing multiple thermoplastic resins, the TPV composition and/or formulation preferably includes more low-MFR thermoplastic resin than high-MFR thermoplastic resin. The low-MFR thermoplastic resin is used to provide viscosity matching during TPV manufacturing for finer vulcanized rubber dispersions whereas the high-MFR thermoplastic resin is employed to provide TPV processability for injection molding and other fabrication techniques that require lower TPV viscosity. For instance, of the combined weight of the low-MFR and high-MFR thermoplastic resin, 51 to 99 wt % is low-MFR, such as 55 to 95 wt %, or 55 wt % to 75 wt %, with the balance being the high-MFR thermoplastic resin.

In summary, then, TPV compositions and/or formulations according to some embodiments include a first (low-MFR) thermoplastic resin and optionally a second (high-MFR) thermoplastic resin, such that the second thermoplastic resin is present at 0 wt % to 49 wt % of the combined amount of first and second thermoplastic resin. Where the second thermoplastic resin is present, it is preferably present within the range of 1 wt % to 49 wt %, such as 5 to 49 wt %, or 10 to 35 wt %, such as 12 to 33 wt %, of the combined amount of first and second thermoplastic resin (with ranges from any of the foregoing lows to any of the foregoing highs, e.g., 1 to 33 wt %, also contemplated in various embodiments).

In the presently disclosed compositions and methods, the thermoplastic resin is an olefinic thermoplastic resin that comprises, or consists of, polypropylene. In preferred embodiments, the thermoplastic component comprises, in some embodiments consists of, an isotactic polypropylene.

Amount of Thermoplastic Component: In many embodiments, the thermoplastic component of a TPV composition and/or TPV formulation makes up from 10 to 40 wt % of the TPV composition and/or TPV formulation, based on the total weight of the TPV formulation, including both of extender and processing oils. Other contemplated ranges include 15 to 30 wt % and 17 to 25 wt %, with ranges from any of the foregoing low ends to any of the foregoing highs ends also contemplated in various embodiments.

Oil

TPVs (and TPV formulations used in making the TPVs) may further comprise oil, including process oil (added to the TPV formulation, as described previously) and/or extender oil (which may be present in the rubber component included in the TPV formulation, also as described previously). The oils that may be used include hydrocarbon oils and plasticizers, such as organic esters and synthetic plasticizers. Many additive oils are derived from petroleum fractions, and have particular ASTM designations depending on whether they fall into the class of paraffinic, naphthenic, or aromatic oils. Other types of additive oils include alpha-olefinic synthetic oils, such as liquid polybutylene. Additive oils other than petroleum based oils can also be used, such as oils derived from coal tar and pine tar, as well as synthetic oils, e.g., polyolefin materials. In particular embodiments, oil included in the TPV is selected based on API groupings (e.g., an API Group I, Group II, Group III, Group IV, or Group V base stock oil may be used as the oil in the TPV). In particular embodiments, oil included in the TPV comprises Group II or higher oil, such as Group II oil (e.g., ParaLux™ 6001R process oil, available from ChevronTexaco Corp.). Also or instead, the oil could include white oil (e.g., pharmaceutical grade oil, such as Primol™ 542 high purity grade white oil, available from ExxonMobil Chemical Company, Baytown, Tex.).

Process oil may be added to a TPV formulation (and/or may be present in a resulting TPV composition) in total amounts ranging from 5 to 200 phr (parts by weight per 100 parts by weight rubber component), preferably 50 to 150 phr, such as 75 to 125 phr, with ranges from any of the foregoing lows to any of the foregoing highs also contemplated in various embodiments. Put in terms of wt %, process oil may be added to the TPV formulation in amounts within the range from 10 to 70 wt %, preferably 20 to 60 wt %, such as 40 to 60 wt %, such weight percentages based on total weight of the TPV formulation, and with ranges from any of the foregoing lows to any of the foregoing highs also contemplated in various embodiments.

Extender oil may be present in the rubber component in amounts within the range from 0 phr to 150 phr, such as 25 to 125 phr, or 50 to 100 phr (0 to 30 wt %, preferably 10 to 25 or 12 to 20 wt %, based on total weight of the TPV formulation), with ranges from any of the foregoing lows to any of the foregoing highs also contemplated.

Total additive oil (extender oil +process oil) may therefore be within the range from 5 to 350 phr (or 5 to 70 wt %) based on total weight of TPV formulation.

Cure Agents

The TPV formulation also includes a vulcanizing agent, which may be at least in part consumed during dynamic vulcanization of the TPV formulation. Any vulcanizing agent that is capable of curing or crosslinking the rubber employed in preparing the TPV may be used. For example, where the rubber includes an olefinic elastomeric copolymer, the cure agent may include peroxides, phenolic resins, free radical curatives, and/or other curatives conventionally employed. In some embodiments, the vulcanizing agent comprises a phenolic resin, and may be, for instance, a phenolic resin-in-oil cure agent (where the oil added with the resin forms part of the process oil added to the TPV formulation during processing). Cure accelerators (e.g., metal halides such as stannous chloride, zinc oxide, and the like) may be used in the TPV formulation in conjunction with the vulcanizing agent. Particularly useful vulcanizing agents, including phenolic resins, and cure accelerators, including stannous chloride, are described in Paragraphs [0046] to [0054] of PCT Application No. PCT/US15/65048, filed Dec. 10, 2015, which description is hereby incorporated by reference. “Curatives” encompasses both vulcanizing agents and curing accelerators.

Curative compositions as described above are typically added to a TPV formulation in an amount of from 0.015 to 0.03 wt % of the TPV formulation, for example from 0.02 to 0.03 or from 0.02 to 0.025 wt %.

Other Additives

The TPV formulations and/or TPV compositions of various embodiments may also include one or more additives, including metal oxides, acid scavengers, reinforcing and non-reinforcing fillers and/or extenders, antioxidants, stabilizers (e.g., UV stabilizers), antiblocking agents, anti-static agents, waxes, foaming agents, pigments, flame retardants, and any other additive, such as processing aids known in the rubber compounding art. In some embodiments, the composition further comprises at least one additive selected from fillers, processing aids, curing accelerators, or combinations thereof.

For example, the TPV composition may include reinforcing and non-reinforcing fillers, antioxidants, stabilizers, antiblocking agents, anti-static agents, waxes, foaming agents, pigments, flame retardants and other processing aids (other than the process oils described above) known in the rubber compounding art. Fillers and extenders that can be utilized include conventional inorganics such as calcium carbonate, clays, silica, talc, titanium dioxide, carbon black, as well as organic and inorganic nanoscopic fillers. Fillers, such as carbon black, may be added as part of a masterbatch, and for example may be added in combination with a carrier such as polypropylene.

In one or more embodiments, the TPV formulation and/or composition includes at least 5, 6, 7, 8, 9, or 10 wt % of one or more fillers, such as calcium carbonate, clays, silica, talc, titanium dioxide, carbon black, and blends thereof, based on the weight of the TPV formulation or composition, as applicable. In preferred embodiments, the TPV formulation and/or composition includes clay and/or carbon black in an amount ranging from a low of any one of 5, 6, 7, 8, 9, or 10 to a high of any one of 15, 16, 17, 18, 19, or 20 wt % based on the total weight of the TPV formulation or TPV composition, as applicable. In one or more embodiments, the TPV composition or formulation comprises antioxidants in an amount less than or equal to 5 wt %, or 4 wt %, or 3 wt %, or 2 wt %, or 1 wt %, or 0.5 wt %, based on the total weight of the TPV composition or formulation.

Compatibilizer

As explained above, incorporating a compatibilizer into the TPV formulation (or composition) provides an improvement in particle size distribution, measured as Dw/Dn and called “particle size dispersity index” (PSDI) with an attendant improvement in some physical properties of the resulting TPV composition. The improvement that is reduction, in PSDI is over and above that achieved by only viscosity matching the rubber and thermoplastic components. In any embodiment, the inventive composition have a Dw/Dn (PSDI) of less than 8, or 7, or 6, or 5, or 4, or 3, or 2.5, or within a range from 1 or 2 to 2.5, or 3, or 4, or 5, or 6, or 7, or 8, alternately from 1 to 8, alternately from 1 to 7, alternately from 1.5 to 6, alternately from 2 to 4, alternately from 2 to 3.

A PEDM compatibilizer is typically added in an amount of from 0.2 to 25 wt % (of the TPV formulation or TPV composition). In some instances, the amount of the compatibilizer is from 0.3 to 25 wt %, or from 0.5 to 25 wt %, or from 1 to 25 wt %, or from 2 to 20 wt % or from 2 to 20 wt % in a TPV formulation or TPV composition.

In a TPV composition or a TPV formulation as presently disclosed, a PEDM compatibilizer can be present in an amount of 1 to 35 wt %, or 2 to 30 wt % or 3 to 25%, of the amount of an EPDM rubber component of the TPV composition or TPV formulation.

In the present disclosure, a propylene-ethylene-diene terpolymer rubber (PEDM) is used as a compatibilizer.

Propylene-Ethylene-Diene Terpolymer

The “propylene-ethylene-diene terpolymer” as used herein may be any polymer comprising ethylene, propylene, a diene and other comonomers, such as butene, styrene or norbornene. The term “polymer” refers to any carbon-containing compound having repeat units from one or more different monomers. Preferably the propylene-ethylene-diene based polymer comprises ethylene-derived units, propylene-derived units, and, optionally, diene-derived units. For example, the propylene-ethylene-diene terpolymer may be an ethylene propylene-α-olefin-diene terpolymer. The propylene-ethylene-diene terpolymers may be prepared by polymerizing ethylene and propylene with one or more dienes.

The other comonomers may be linear or branched. Preferred linear comonomers include C₄ to C₈ α-olefins, more preferably 1-butene, 1-hexene, and 1-octene, even more preferably ethylene or propylene. Preferred branched comonomers include 4-methyl-1-pentene, 3-methyl-1-pentene, 2-ethyl-1-butene, and 3,5,5 -trimethyl-1-hexene. In one or more embodiments, the comonomers may include styrene or norbornene.

The dienes may be conjugated or non-conjugated. Preferably, the dienes are non-conjugated. Illustrative dienes may include, but are not limited to, 5-ethylidene-2-norbornene (ENB); 1,4-hexadiene; 5-methylene-2-norbornene (MNB); 1,6-octadiene; 5-methyl-1,4-hexadiene; 3,7-dimethyl-1,6-octadiene; 1,3-cyclopentadiene; 1,4-cyclohexadiene; vinyl norbornene (VNB); dicyclopendadiene (DCPD); and combinations thereof. Preferably, the diene is ENB or VNB.

The propylene-ethylene-diene terpolymer may have an ethylene amount of from 2 wt % by weight to 25 wt % by weight of the PEDM terpolymer, or from 5 wt % to 25 wt %, or from 7 wt % to 25 wt %, or from 10 wt % to 25 wt %, based on the weight of the PEDM polymer. The balance of the propylene-ethylene-diene terpolymer comprises propylene and, optionally, one or more dienes.

Preferably, the propylene-ethylene-diene terpolymer comprises a diene content of from 1 wt % to 21 wt % based on the weight of the PEDM polymer, or from 1.5 wt % to 15 wt %, or from 2 wt % to 15 wt %, or 3 wt % to 10 wt %, or from 3 wt % to 8 wt %, based on the weight of the PEDM polymer. Other useful ranges include from 1 wt % to 18 wt %, or from 1 wt % to 15 wt %, or from 1 wt % to 10 wt %, or from 3 wt % to 12 wt %, or from 4 wt % to 12 wt % based on the weight of the PEDM polymer. In one or more embodiments, the propylene-ethylene-diene terpolymer may comprise 5-ethylidene-2-norbornene in an amount of from 1 wt % to 21 wt %, or from 1.5 wt % to 15 wt %, or from 3 wt % to 20 wt %, or from 3 wt % to 18 wt %, or from 3 wt % to 15 wt %, based on the weight of the PEDM polymer.

A PEDM used in the TPV presently disclosed can be one including 5 to 18% ethylene and 2 to 12 wt % ethylene norbornene-derived units by weight of the PEDM.

The propylene-ethylene-diene terpolymer may have a weight average molecular weight (Mw) of 5,000,000 g/mol or less, a number average molecular weight (Mn) of 3,000,000 g/mol or less, a z-average molecular weight (Mz) of 10,000,000 g/mol or less, and a g′ index (also referred to as a branching index) of 0.95 or greater measured at the weight average molecular weight (Mw) of the polymer using isotactic polypropylene as the baseline, all of which may be determined by size exclusion chromatography as described below. The propylene-ethylene-diene terpolymer may have an Mn of from 5,000 to 5,000,000 g/mole, or from 10,000 to 1,000,000 g/mole, or from 20,000 to 500,000 g/mole, or from 30,000 to 400,000 g/mole.

The molecular weight distribution index (MWD=(Mw/Mn)), sometimes referred to as a “polydispersity index” (PDI), of the propylene-ethylene-diene terpolymer may be from 1.2 to 40. For example, the propylene-ethylene-diene terpolymer may have an MWD with an upper limit of 40, or 20, or 10, or 9, or 7, or 5, and a lower limit of 1.2, or 1.5, or 1.7. In one or more embodiments, the MWD of the propylene-ethylene-diene terpolymer is 1.5 to 7, or from 1.7 to 5.

The propylene-ethylene-diene terpolymer may have a g′ index value of 0.95 or greater, or at least 0.98, or at least 0.99, wherein g′ is measured at the Mw of the polymer using the intrinsic viscosity of isotactic polypropylene as the baseline. For use herein, the g′ index is defined as:

${g^{\prime} = \frac{\eta_{b}}{\eta_{l}}},$

where η_(b) is the intrinsic viscosity of the propylene-ethylene-diene terpolymer and η₁ is the intrinsic viscosity of a linear propylene polymer of the same viscosity-averaged molecular weight (M_(v)) as the propylene-ethylene-diene terpolymer. Thus, η₁=KM_(v) ^(α), where K and α are measured values for linear polymers and unless otherwise indicated, α=0.705 and K=0.0002288 for linear propylene polymers.

The propylene-ethylene-diene terpolymer may have a density of from 0.83 g/cm³ to 0.92 g/cm³, or from 0.85 g/cm³ to 0.91 g/cm³, or from 0.85 g/cm³ to 0.90 g/cm³, at 23° C. as measured per the ASTM D-1505 test method.

The propylene-ethylene-diene terpolymer may have a melt flow rate (MFR, 2.16 kg weight at 230° C.), equal to or greater than 0.2 g/10 min as measured according to the ASTM D-1238. Preferably, the MFR (2.16 kg at 230° C.) is from 0.2 g/10 min to 200 g/10 min, or from 0.2 g/10 min to 100 g/10 min, or from 0.2 g/10 min to 50 g/10 min, or from 0.2 g/10 min to 30 g/10 min, or from 0.2 g/10 min to 25 g/10 min, or from 0.5 g/10 min to 25 g/10 min

The propylene-ethylene-diene terpolymer may have a Mooney viscosity ML (1+4) at 125° C., as determined according to ASTM D1646, of greater than 5, or greater than 10, or greater than 15, or greater than 20, or 5 to 100, alternately 10 to 80.

The propylene ethylene diene copolymer is essentially devoid of crystallinity. Crystallinity for these statistical propylene ethylene copolymers with a predominant amount of propylene arises for catenated propylene residues, there is too little ethylene to have significant amount of catenated ethylene residues and thus crystallinity for ethylene sequences. Crystallinity in propylene residue catenation in polyolefins arises from the relative orientation of the pendant methyl groups on the alternate carbon atoms. Sequences of exclusive meso orientation or predominantly meso lead to isotactic crystallinity, sequences of random with mixtures meso and rac orientation lead to an absence of crystallinity: all at similar compositions and sequence distribution of the statistical propylene ethylene copolymers. The control of the meso or mixed orientation of the methyl groups is determined by the conditions for the synthesis typically the catalyst used and the polymerization conditions. The propylene ethylene copolymers of this invention are essentially devoid of crystallinity, preferably completely so as determined by DSC, by reason of having all of the catenated propylene residues in random orientations of meso and racemic. The determination of crystallinity in copolymers is difficult since in addition to the changes in the meso/random orientation of the propylene residues and the degrees of catenation, the absolute values of crystallinity are diluted by comingling with ethylene residues. Without wishing to be bound by theory, it is thought that when the propylene ethylene copolymers are made under the identical polymerization conditions, including catalysts, that even in the absence of ethylene or diene comonomers, the homo polypropylene made would be a mixture of random and meso orienataion of the methyl residues and would thus have essentially no crystallinity as measured for this poly propylene by DSC. An alternate method would be consider the ratio of the heat of fusion of the copolymer, propylene ethylene diene to the corresponding polypropylene made under the same conditions. For this propylene ethylene diene copolymers this ration cannot be experimentally determined, therefore a the heat of fusion for the linear PEDM is set at 207 J/g.

The propylene-ethylene-diene terpolymer may have a heat of fusion (H_(f)) determined by the DSC procedure described herein, which is greater than or equal to 0 Joules per gram (J/g), and is less than 2 J/g. The propylene-ethylene-diene terpolymer may have a heat of fusion (H_(f)) determined by the DSC procedure described herein which is undetectable or greater than or equal to 0 Joules per gram (J/g), and less than 2 J/g, or equal to or less than 1.5 J/g, or equal to or less than 1 J/g. Preferred propylene-ethylene-diene terpolymers are amorphous having no detectable heat of fusion by DSC. By “undetectable heat of fusion” is meant that there is no measureable thermal output during the DSC heating cycle (described below).

The crystallinity of the propylene-ethylene-diene terpolymer may be expressed in terms of percentage of crystallinity (i.e., % crystallinity), as determined according to the DSC procedure described below. The propylene-ethylene-diene terpolymer may have a % crystallinity of less than 15%, or less than 10%, or less than 5%, or less than 3%, or less than 1%. In some embodiments, the propylene-ethylene-diene terpolymer may have a % crystallinity of from 0% to 3%, or from 0.05% to 3%, or from 0.1% to 3%. In one or more embodiments, the propylene-ethylene-diene terpolymer may have crystallinity of less than 3%, or from 0.25% to 3%, or from 0.5% to 3%, or from 0.75% to 2%. (The degree of crystallinity (%) is determined by dividing heat of fusion (in J/g) measured by the heat of fusion for 100% crystalline polypropylene which has the value of 207 J/g (B. Wunderlich, Thermal Analysis, Academic Press, 1990, pp. 417-431) and multiplying by 100. Preferred propylene-ethylene-diene terpolymers are amorphous having a nondetectable heat of fusion, and thus a non-calculable % crystallinity, by DSC.

The propylene-ethylene-diene terpolymer preferably may have a single broad melting transition. However, the propylene-ethylene-diene terpolymer may show secondary melting peaks adjacent to the principal peak, but for purposes herein, such secondary melting peaks are considered together as a single melting point, with the highest of these peaks (relative to baseline as described herein) being considered as the melting point of the propylene-ethylene-diene terpolymer. PEDM terpolymers are typically amorphous.

The propylene-ethylene-diene terpolymer may have a melting point, as measured by the DSC procedure described herein, of equal to or less than 100° C., or less than 90° C., or less than 80° C., or less than or equal to 75° C. In one or more embodiments, the propylene-ethylene-diene terpolymer may have a melting point of from 10° C. to 80° C., or from 15° C. to 75° C., or from 20° C. to 70° C. In one or more embodiments, the propylene-ethylene-diene terpolymer may not have a melting point and is amorphous.

The propylene-ethylene-diene terpolymer can have a glass transition (Tg) range, as determined by the DSC procedure described herein, from −25° C. to −2° C., or from −20° C. to −2° C., or from −15° C. to −2° C., or from −10° C. to −2° C.

The Differential Scanning Calorimetry (DSC) procedure may be used to determine heat of fusion, glass transition range, and melting temperature of the propylene-ethylene-diene terpolymer. The method is as follows: approximately 6 mg of material placed in microliter aluminum sample pan. The sample is placed in a Differential Scanning Calorimeter (Perkin Elmer or TA Instrument Thermal Analysis System) and is heated from ambient to 210° C. at 10° C./minute and held at 210° C. for 5 minutes. Afterward, the sample is cooled down to −40° C. at 10° C./minute and this cooling curve is used to measure the Tg. The sample is held at −40° C. for 5 minutes and then heated from −40° C. to 210° C. at 10° C./minute. During the second heating cycle, appearance of melting indicates crystallinity and thus measured heat of fusion is used to compute the crystallinity. The thermal output, recorded as the area under the melting peak of the sample, is a measure of the heat of fusion and is expressed in Joules per gram of polymer. The melting point is recorded as the temperature of the greatest heat absorption within the range of melting of the sample relative to a baseline measurement for the increasing heat capacity of the polymer as a function of temperature.

The propylene-ethylene-diene terpolymer may be a blend of discrete random propylene-ethylene-diene terpolymers as long as the polymer blend has the properties of the propylene-ethylene-diene terpolymer as described herein. The number of propylene-ethylene-diene terpolymers may be three or less, or two or less. In one or more embodiments, the propylene-ethylene-diene terpolymer may include a blend of two propylene-ethylene-diene terpolymers differing in the olefin content, the diene content, or the both. Preparation of such polymer blends may be found in US 2004/0024146 and US 2006/0183861, both hereby incorporated by reference in their entirety.

The PEDM copolymers useful herein may also be prepared using an indecenyl catalyst compound in combination with an activator, and an optional support, as further described in concurrently filed applications: 1) U.S. Ser. No. ______, entitled “Processes for Producing High Propylene Content PEDM using Tetrahydroindacenyl Catalyst Systems”, attorney docket number (2018EM053/2), which claims priority to and the benefit of U.S. Ser. No. 62/644,971, filed Mar. 19, 2018; and 2) U.S. Ser. No. ______, entitled “Processes for Producing High Propylene Content PEDM Having Low Glass Transition Temperatures Using Tetrahydroindacenyl Catalyst Systems”, attorney docket number (2018EM053A); which claims priority to and the benefit of U.S. Ser. No. 62/644,971, filed Mar. 19, 2018.

The catalyst compound, optional support and activator may be combined in any order, and are combined typically prior to contacting the catalyst system with the monomer. In at least one embodiment, the catalyst compound is represented by formula (I):

T_(y)Cp′_(m)MG_(n)X_(q)  (I)

wherein:

-   Cp′ is a tetrahydroindacenyl group (such as tetrahydro-s-indacenyl     or tetrahydro-as-indacenyl) which is optionally substituted or     unsubstituted, provided that when Cp′ is tetrahydro-s-indacenyl: 1)     the 3 and/or 4 positions are not aryl or substituted aryl, 2) the 3     position is not directly bonded to a group 15 or 16 heteroatom, 3)     there are no additional rings fused to the tetrahydroindacenyl     ligand, 4) T is not bonded to the 2-position, and 5) the 5, 6, or     7-position (preferably the 6 position) is geminally disubstituted,     preferably with two C₁-C₁₀ alkyl groups; M is a group 2, 3, 4, 5, or     6 transition metal, preferably group 4 transition metal, for example     titanium, zirconium, or hafnium (preferably titanium); -   T is a bridging group (such as dialkylsilylene, dialkylcarbylene,     phen-1,2-diyl, substituted phen-1,2-diyl, cyclohex-1,2-diyl or     substituted cyclohex-1,2-diyl). T is preferably (CR⁸R⁹)_(x), SiR⁸R⁹     or GeR⁸R⁹ where x is 1 or 2, R⁸ and R⁹ are independently selected     from hydrogen, substituted or unsubstituted hydrocarbyl, halocarbyl,     silylcarbyl and germylcarbyl and R⁸ and R⁹ may optionally be bonded     together to form a ring structure, and in a particular embodiment,     R⁸ and R⁹ are not aryl); -   y is 0 or 1, indicating the absence or presence of T; -   G is a heteroatom group represented by the formula JR_(z-y) ^(i)     where J is N, P, O or S, R′ is a C₁ to C₁₀₀ hydrocarbyl group (such     as a C₁ to C₂₀ hydrocarbyl group), and z is 2 when J is N or P, and     z is 1 when J is O or S (preferably J is N and z is 2) (R^(i) can be     a linear, branched or cyclic C₁ to C₂₀ hydrocarbyl group, preferably     independently selected from methyl, ethyl, propyl, butyl, pentyl,     hexyl, heptyl, octyl, nonyl, decyl, phenyl, and isomers thereof,     including t-butyl, cyclododecyl, cyclooctyl, preferably t-butyl and     or cyclododecyl); -   X is a leaving group (such as a halide, a hydride, an alkyl group,     an alkenyl group or an arylalkyl group) and optionally two or more X     may form a part of a fused ring or a ring system; m=1; n =1, 2 or 3;     q=1, 2 or 3; and the sum of m+n+q is equal to the oxidation state of     the transition metal (preferably 3, 4, 5, or 6, preferably 4);     preferably m=1, n=1, q is 2, and y=1.

In at least one embodiment of formula (I), M is a group 4 transition metal (preferably Hf, Ti and/or Zr, preferably Ti). In at least one embodiment of formula (I), JR'_(z-y) ^(i) is cyclododecyl amido, t-butyl amido, and or 1-adamantyl amido.

In at least one embodiment of formula (I), each X is, independently, selected from hydrocarbyl radicals having from 1 to 20 carbon atoms, aryls, hydrides, amides, alkoxides, sulfides, phosphides, halides, dienes, amines, phosphines, ethers, and a combination thereof, (two X's may form a part of a fused ring or a ring system), preferably each X is independently selected from halides, aryls and C₁ to C₅ alkyl groups, preferably each X is a benzyl, methyl, ethyl, propyl, butyl, pentyl, or chloro group.

In at least one embodiment of formula (I), the Cp' group may be substituted with a combination of substituent groups R. R includes one or more of hydrogen, or linear, branched alkyl radicals, or alkenyl radicals, alkynyl radicals, cycloalkyl radicals or aryl radicals, acyl radicals, alkoxy radicals, aryloxy radicals, alkylthio radicals, dialkylamino radicals, alkoxycarbonyl radicals, aryloxycarbonyl radicals, carbamoyl radicals, alkyl- or dialkyl-carbamoyl radicals, acyloxy radicals, acylamino radicals, arylamino radicals, straight, branched or cyclic, alkylene radicals, or combination thereof. In at least one embodiment, substituent groups R have up to 50 non-hydrogen atoms, preferably from 1 to 30 carbon, that can also be substituted with halogens or heteroatoms or the like, provided that when Cp′ is tetrahydro-s-indacenyl: 1) the 3 and/or 4 position is not aryl or substituted aryl, 2) the 3-position is not substituted with a group 15 or 16 heteroatom, 3) there are no additional rings fused to the tetrahydroindacenyl ligand, T is not bonded to the 2-position, and 5) the 5, 6, or 7-position (preferably the 6 position) is geminally disubstituted, preferably with two C₁-C₁₀ alkyl groups. Non-limiting examples of alkyl substituents R include methyl, ethyl, propyl, butyl, pentyl, hexyl, cyclopentyl, cyclohexyl, benzyl or phenyl groups and the like, including all their isomers, for example, tertiary butyl, isopropyl and the like. Other hydrocarbyl radicals include fluoromethyl, fluoroethyl, difluoroethyl, iodopropyl, bromohexyl chlorobenzyl and hydrocarbyl substituted organometalloid radicals including trimethylsilyl, trimethylgermyl, methyldiethylsilyl and the like; and halocarbyl-substituted organometalloid radicals including tris(trifluoromethyl)silyl, methylbis(difluoromethyl)silyl, bromomethyldimethylgermyl and the like; and disubstituted boron radicals including dimethylboron for example; and disubstituted pnictogen radicals including dimethylamine, dimethylphosphine, diphenylamine, methylphenylphosphine, chalcogen radicals including methoxy, ethoxy, propoxy, phenoxy, methylsulfide and ethylsulfide. Non-hydrogen substituents R include the atoms carbon, silicon, boron, aluminum, nitrogen, phosphorus, oxygen, tin, sulfur, germanium and the like, including olefins such as, but not limited to, olefinically unsaturated substituents including vinyl-terminated ligands, for example but-3-enyl, prop-2-enyl, hex-5-enyl and the like.

In at least one embodiment of formula (I), the substituent(s) R are, independently, hydrocarbyl groups, heteroatoms, or heteroatom containing groups, such as methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl or an isomer thereof, or a C₁ to C₂₀ hydrocarbyl substituted with an N, O, S and or P heteroatom or heteroatom containing group (typically having up to 12 atoms, including the N, O, S and P heteroatoms), provided that when Cp′ is tetrahydro-s-indacenyl, the 3 and/or 4 position are not aryl or substituted aryl, the 3 position is not substituted with a group 15 or 16 heteroatom, and there are no additional rings fused to the tetrahydroindacenyl ligand, T is not bonded to the 2-position, and the 5, 6, or 7-position (preferably the 6 position) is geminally disubstituted, preferably with two C₁-C₁₀ alkyl groups.

In at least one embodiment of formula (I), the Cp′ group is tetrahydro-as-indacenyl or tetrahydro-s-indacenyl which may be substituted.

In at least one embodiment of formula (I), y is 1, and T is a bridging group containing at least one group 13, 14, 15, or 16 element, in particular boron or a group 14, 15 or 16 element. Examples of suitable bridging groups include P(═S)R*, P(═Se)R*, P(═O)R*, R*₂C, R*₂Si, R*₂Ge, R*₂CCR*₂, R*₂CCR*₂CR*₂, R*₂CCR*₂CR*₂CR*₂, R*C═CR*, R*C═CR*CR*₂, R*₂CCR*═CR*CR*₂, R*C═CR*CR*═CR*, R*C═CR*CR*₂CR*₂, R*₂CSiR*₂, R*₂SiSiR*₂, R*₂SiOSiR*₂, R*₂CSiR*₂CR*₂, R*₂SiCR*₂SiR*₂, R*C═CR*SiR*₂, R*₂CGeR*₂, R*₂GeGeR*₂, R*₂CGeR*₂CR*₂, R*₂GeCR*₂GeR*₂, R₂SiGeR*₂, R*C═CR*GeR*₂, R*B, R*₂C, R*₂C—BR*—CR*₂, R*₂C*—CR*₂, R*₂CR*₂C—O—CR*₂CR*₂, R*₂C O—CR*₂CR*₂, R*₂C—O—CR*═CR*, R*₂C—S—CR*₂, R*₂CR*2C—S—CR*₂CR*₂, R*₂C—S—CR*₂CR*₂, R*₂—S—CR*═CR*, R*₂C—Se—CR*₂, R*₂CR*₂C—Se—CR*₂CR*₂, R*₂C—Se—CR*₂CR*₂, R*₂—Se—CR*═CR*, R*₂C—N═CR*, R*₂C—NR*—CR*₂, R*₂C—NR*—CR*₂CR*₂, R*₂C—NR*—CR*═CR*, R*₂CR*₂C—NR*—CR*₂CR*₂, R*₂C—P═CR*, R*₂C—PR*—CR*₂, O, S, Se, Te, NR*, PR*, AsR*, SbR*, O—O, S—S, R*N—NR*, R*P—PR*, O—S, O—NR*, O—PR*, S—NR*, S—PR*, and R*N—PR* where R* is hydrogen or a C₁-C₂₀ containing hydrocarbyl, substituted hydrocarbyl, halocarbyl, substituted halocarbyl, silylcarbyl or germylcarbyl substituent, and optionally two or more adjacent R* may join to form a substituted or unsubstituted, saturated, partially unsaturated or aromatic, cyclic or polycyclic substituent, and optionally any one or more adjacent R* and R^(i) may join to form a substituted or unsubstituted, saturated, partially unsaturated or aromatic, cyclic or polycyclic substituent. Preferred examples for the bridging group T include —CH₂—, —CH₂CH₂—, —SiMe₂—, —Si(Me)(Ph)—, —Si(CH₂)₃—, —Si(CH₂)₄—, —O—, —S—, —N(Ph)—P(Ph)—, —N(Me)—, —P(Me)—, —N(Et)—, —N(Pr)—, —N(Bu)—, —P(Et)—, —P(Pr)—, —(Me)₂SiOSi(Me)₂—, and —P(Bu)—. In a preferred embodiment of the present disclosure, when Cp′ is tetrahydro-s-indacenyl and T is R*₂Si, then R* is not aryl. In some embodiments, R* is not aryl or substituted aryl.

In at least one embodiment, the catalyst compound is one or more bridged transition metal compounds represented by formula (III):

where M is a group 4 metal (such as Hf, Ti or Zr, preferably Ti);

-   J N, O, S or P; -   p is 2 when J is N or P, and is 1 when J is O or S (preferably J is     N, y=1, and p=2); -   each R^(a), R^(b), R^(c) , R^(d), R^(e) and R^(f) are independently     hydrogen or a C₁-C₁₀ alkyl (alternately a C₂-C₁₀ alkyl); -   each R², R⁴, R³, R⁶, and R⁷ is independently hydrogen, or a C₁-C₅₀     substituted or unsubstituted hydrocarbyl, halocarbyl, silylcarbyl or     germylcarbyl; -   each R′ is, independently, a C₁-C₁₀₀ substituted or unsubstituted     hydrocarbyl, halocarbyl, silylcarbyl or germylcarbyl; -   T is a bridging group and y is 0 or 1 indicating the absence (y=0)     or presence (y=1) of T; -   and each X is, independently, a leaving group, or two Xs are joined     and bound to the metal atom to form a metallocycle ring, or two Xs     are joined to form a chelating ligand, a diene ligand, or an     alkylidene.

In some embodiments of formulae II and III, y is 1 and T is (CR⁸R⁹)_(x), SiR⁸R⁹ or GeR⁸R⁹ where x is 1 or 2, R⁸ and R⁹ are independently selected from hydrogen or substituted or unsubstituted hydrocarbyl, halocarbyl, silylcarbyl and germylcarbyl and R⁸ and R⁹ may optionally be bonded together to form a ring structure.

In at least one embodiment of the present disclosure, each R², R³, R⁶, and R⁷ is independently hydrogen, or a C₁-C₅₀ substituted or unsubstituted hydrocarbyl, halocarbyl, silylcarbyl or germylcarbyl, preferably methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, and dodecyl or an isomer thereof.

In at least one embodiment of the present disclosure, each R², R³, R⁴, and R⁷ is independently hydrogen, or a C₁-C₅ substituted or unsubstituted hydrocarbyl, halocarbyl, silylcarbyl or germylcarbyl, preferably methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, and dodecyl or an isomer thereof.

In at least one embodiment of the present disclosure, each R^(a) or R^(d) is independently selected from methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, and isomers thereof, preferably methyl and ethyl, preferably methyl.

In at least one embodiment of the present disclosure, each R^(b), R^(c), R^(e) or R^(f) is independently selected from hydrogen, methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, and isomers thereof, preferably hydrogen or methyl, preferably hydrogen.

In at least one embodiment of the present disclosure, each Ra is independently selected from methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, and isomers thereof, preferably methyl and ethyl, preferably methyl, and each R^(b) and R^(c) are independently selected from hydrogen, methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, and isomers thereof, preferably hydrogen or methyl, preferably hydrogen.

In at least one embodiment of the present disclosure, each R^(d) is independently selected from hydrogen, methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, and isomers thereof, preferably methyl and ethyl, preferably methyl, and each R^(e) and R^(f) are independently selected from hydrogen, methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, and isomers thereof, preferably hydrogen or methyl, preferably hydrogen.

In at least one embodiment of the present disclosure, each R^(a), R^(b) and R^(c) are independently selected from hydrogen, methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, and isomers thereof, preferably hydrogen or methyl.

In at least one embodiment of the present disclosure, each R^(d), R^(e) and R^(f) are independently selected from hydrogen, methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, and isomers thereof, preferably hydrogen or methyl.

In at least one embodiment of the present disclosure, R′ is a C₁-C₁₀₀ substituted or unsubstituted hydrocarbyl, halocarbyl, or silylcarbyl, preferably methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, phenyl or an isomer thereof, preferably t-butyl, neopentyl, cyclohexyl, cyclooctyl, cyclododecyl, adamantyl, or norbornyl.

In at least one embodiment of the present disclosure, T is CR⁸R⁹, R⁸R⁹C-CR⁸R⁹, SiR⁸R⁹ or GeR⁸R⁹ where R⁸ and R⁹ are independently selected from hydrogen or substituted or unsubstituted hydrocarbyl, halocarbyl, silylcarbyl and R⁸ and R⁹ may optionally be bonded together to form a ring structure, preferably each R⁸ and R⁹ is independently methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, benzyl, phenyl, methylphenyl or an isomer thereof, preferably methyl, ethyl, propyl, butyl, or hexyl. When R⁸ and R⁹ are optionally bonded together preferred bridges include substituted or unsubstituted phen-1,2-diyl, cyclohex-1,2-diyl, cyclopentamethylenesilylene, cyclotetramethylenesilylene, cyclotrimethylenesilylene and dibenzo[b,d]silolyl. Additionally, optionally any one or more adjacent R⁸ and/or R⁹ may join to form a substituted or unsubstituted, saturated, partially unsaturated or aromatic, cyclic or polycyclic substituent along with R′.

In at least one embodiment of the present disclosure, at least one of R⁸ or R⁹ is not aryl. In at least one embodiment of the present disclosure, R⁸ is not aryl. In at least one embodiment of the present disclosure, R⁹ is not aryl. In at least one embodiment of the present disclosure, R⁸ and R⁹ are not aryl.

In at least one embodiment of the present disclosure, R⁸ and R⁹ are independently C₁-C₁₀ alkyl, such as methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, or an isomer thereof.

In at least one embodiment of the present disclosure, each R², R³, R⁴, and R⁷ is independently hydrogen or hydrocarbyl. Each R², R³, R⁴, and R⁷ can be independently hydrogen or a C₁-C₁₀ alkyl, such as methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, or an isomer thereof.

In at least one embodiment of the present disclosure, each R², R³, R⁶, and R⁷ is independently hydrogen or hydrocarbyl. Each R², R³, R⁶, and R⁷ can be independently hydrogen or a C₁-C₁₀ alkyl, preferably methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, or an isomer thereof.

In at least one embodiment of the present disclosure, R² is a C₁-C₁₀ alkyl and R³, R⁴, and R⁷ are hydrogen.

In at least one embodiment of the present disclosure, R² is a-Cio alkyl and R³, R⁶, and R⁷ are hydrogen.

In at least one embodiment of the present disclosure, R², R³, R⁴, and R⁷ are hydrogen. In at least one embodiment of the present disclosure, R², R³, R⁶, and R⁷ are hydrogen.

In at least one embodiment of the present disclosure, R² is methyl, ethyl, or an isomer of propyl, butyl, pentyl or hexyl, and R³, R⁴, and R⁷ are hydrogen. In at least one embodiment of the present disclosure, R² is methyl, ethyl, or an isomer of propyl, butyl, pentyl or hexyl, and R³, R⁶, and R⁷ are hydrogen.

In at least one embodiment of the present disclosure, R² is methyl and R³, R⁴, and R⁷ are hydrogen. In at least one embodiment of the present disclosure, R² is methyl and R³, R⁶, and R⁷ are hydrogen.

In at least one embodiment of the present disclosure, R³ is hydrogen. In at least one embodiment of the present disclosure, R² is hydrogen.

In at least one embodiment of the present disclosure, R² and each R^(a) is independently a C₁-C₁₀ alkyl and R³, R⁴, R⁷ and each R⁶ and R^(c) are hydrogen.

In at least one embodiment of the present disclosure, R² and each R^(d) is a C₁-C₁₀ alkyl and R³, R⁶, R⁷ and each R^(e) and R^(f) are hydrogen.

In at least one embodiment of the present disclosure, R² and each R^(d) is independently a methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, or an isomer thereof, and R³, R⁴, R⁷ and each R^(b) and R^(c) are hydrogen.

In at least one embodiment of the present disclosure, R² and each R^(d) is a methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, or an isomer thereof, and R³, R⁶, R⁷ and each R^(e) and R^(f) are hydrogen.

In at least one embodiment of the present disclosure, R′ is C₁-C₁₀₀ or C₁-C₃₀ substituted or unsubstituted hydrocarbyl.

In at least one embodiment of the present disclosure, R′ is C₁-C₃₀ substituted or unsubstituted alkyl (linear, branched, or cyclic), aryl, alkaryl, or heterocyclic group. In at least one embodiment of the present disclosure, R is C₁-C₃₀ linear, branched or cyclic alkyl group.

In at least one embodiment of the present disclosure, R′ is methyl, ethyl, or any isomer of propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, or dodecyl. In at least one embodiment of the present disclosure, R′ is a cyclic or polycyclic hydrocarbyl.

In at least one embodiment of the present disclosure, R′ is selected from tert-butyl, neopentyl, cyclohexyl, cycloheptyl, cyclooctyl, cyclononyl, cyclodecyl, cycloundecyl, cyclododecyl, adamantyl, and norbornyl. In at least one embodiment, R′ is tert-butyl.

In at least one embodiment of the present disclosure, R′ is selected from tert-butyl, neopentyl, cyclohexyl, cycloheptyl, cyclooctyl, cyclononyl, cyclodecyl, cycloundecyl, cyclododecyl, adamantyl, and norbornyl. In at least one embodiment, R^(i) is tert-butyl.

In at least one embodiment of the present disclosure, T is selected from diphenylmethylene, dimethylmethylene, 1,2-ethylene, phen-1,2-diyl, cyclohex-1,2-diyl cyclotrimethylenesilylene, cyclotetramethylenesilylene, cyclopentamethylenesilylene, dibenzo[b,d]silolyl, dimethylsilylene, diethylsilylene, methylethylsilylene, and dipropylsilylene.

In at least one embodiment of the present disclosure, each R^(a) is independently methyl, ethyl, propyl, butyl, pentyl or hexyl. In at least one embodiment of the present disclosure, each R^(a) is independently methyl or ethyl. Each R^(a) can be methyl.

In at least one embodiment of the present disclosure, each R^(d) is independently methyl, ethyl, propyl, butyl, pentyl or hexyl. In at least one embodiment of the present disclosure, each R^(d) is independently methyl or ethyl. Each R^(d) can be methyl.

In at least one embodiment of the present disclosure, each R^(d) and each R^(e) and R^(f) are independently hydrogen, methyl, ethyl, propyl, butyl, pentyl or hexyl. In at least one embodiment of the present disclosure, each R^(d) is independently hydrogen, methyl, or ethyl.

In at least one embodiment of the present disclosure, each R^(b) and R^(c) is hydrogen. In at least one embodiment of the present disclosure, each R^(e) and R^(f) is hydrogen.

In at least one embodiment of the present disclosure, each X is hydrocarbyl, halocarbyl, or substituted hydrocarbyl or halocarbyl.

In at least one embodiment of the present disclosure, X is methyl, benzyl, or halo where halo includes fluoro, chloro, bromo and iodido.

In at least one embodiment of the present disclose, both X are joined together to form a C₄-C₂₀ diene ligand such as 1,3-butadiene, 1,3-pentadiene, 2-methyl-1,3-pentadiene, 2,4-dimethylpentadiene and the like.

In at least one embodiment of formula (II) of the present disclosure: 1) R³ and/or R⁴ are not aryl or substituted aryl, 2) R³ is not directly bonded to a group 15 or 16 heteroatom, and 3) adjacent R⁴, R^(c), R^(a) or R⁷ do not join together to form a fused ring system, and 4) each R^(a) is a C₁ to C₁₀ alkyl (preferably methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, or an isomer thereof).

In a preferred embodiment of the present disclosure, T of any of formulas (I) to (III) is represented by the formula ER^(g) ₂ or (ER^(g) ₂)₂, where E is C, Si, or Ge, and each R^(g) is, independently, hydrogen, halogen, C₁ to C₂₀ hydrocarbyl (such as methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, or dodecyl) or a C₁ to C₂₀ substituted hydrocarbyl, and two R^(g) can form a cyclic structure including aromatic, partially saturated, or saturated cyclic or fused ring system. Preferably, T is a bridging group comprising carbon or silica, such as dialkylsilyl, preferably T is selected from —CH₂—, —CH₂CH₂—, —C(CH₃)₂—, Si(Me)₂, cyclotrimethylenesilylene (—Si(CH₂)₃—), cyclopentamethylenesilylene (—Si(CH₂)₅—) and cyclotetramethylenesilylene (—Si(CH₂)₄—).

In at least one embodiment, a catalyst compound is one or more of:

-   dimethylsilylene(2,6,6-trimethyl-1,5,6,7-tetrahydro-s-indacen-1-yl)(t-butylamido)M(R)₂; -   dimethylsilylene(6,6-dimethyl-1,5,6,7-tetrahydro-s-indacen-1-yl)(t-butylamido)M(R)₂; -   dimethylsilylene(2,7,7-trimethyl-3,6,7,8-tetrahydro-as-indacen-3-yl)(t-butylamido)M(R)₂; -   dimethylsilylene(7,7-dimethyl-3,6,7,8-tetrahydro-as-indacen-3-yl)(t-butylamido)M(R)₂; -   dimethylsilylene(2,6,6-trimethyl-1,5,6,7-tetrahydro-s-indacen-1-yl)(cyclododecylamido)M(R)₂; -   dimethylsilylene(6,6-dimethyl-1,5,6,7-tetrahydro-s-indacen-1-yl)(cyclododecylamido)M(R)₂; -   dimethylsilylene(2,7,7-trimethyl-3,6,7,8-tetrahydro-as-indacen-3-yl)(cyclododecylamido)M(R)₂; -   dimethylsilylene(7,7-dimethyl-3,6,7,8-tetrahydro-as-indacen-3-yl)(cyclododecylamido)M(R)₂; -   dimethylsilylene(2,6,6-trimethyl-1,5,6,7-tetrahydro-s-indacen-1-yl)(cyclohexylamido)M(R)₂; -   dimethylsilylene(6,6-dimethyl-1,5,6,7-tetrahydro-s-indacen-1-yl)(cyclohexylamido)M(R)₂; -   dimethylsilylene(2,7,7-trimethyl-3,6,7,8-tetrahydro-as-indacen-3-yl)(cyclohexylamido)M(R)₂; -   dimethylsilylene(7,7-dimethyl-3,6,7,8-tetrahydro-as-indacen-3-yl)(cyclohexylamido)M(R)₂; -   dimethylsilylene(2,6,6-trimethyl-1,5,6,7-tetrahydro-s-indacen-1-yl)(adamantylamido)M(R)₂; -   dimethylsilylene(6,6-dimethyl-1,5,6,7-tetrahydro-s-indacen-1-yl)(adamantylamido)M(R)₂; -   dimethylsilylene(2,7,7-trimethyl-3,6,7,8-tetrahydro-as-indacen-3-yl)(adamantylamido)M(R)₂; -   dimethylsilylene(7,7-dimethyl-3,6,7,8-tetrahydro-as-indacen-3-yl)(adamantylamido)M(R)₂; -   dimethylsilylene(2,6,6-trimethyl-1,5,6,7-tetrahydro-s-indacen-1-yl)(neopentylamido)M(R)₂; -   dimethylsilylene(6,6-dimethyl-1,5,6,7-tetrahydro-s-indacen-1-yl)(neopentylamido)M(R)₂; -   dimethylsilylene(2,7,7-trimethyl-3,6,7,8-tetrahydro-as-indacen-3-yl)(neopentylamido)M(R)₂; -   dimethylsilylene(7,7-dimethyl-3,6,7,8-tetrahydro-as-indacen-3-yl)(neopentylamido)M(R)₂; -   dimethylsilylene(2-methyl-6,6-diethyl-1,5,6,7-tetrahydro-s-indacen-1-yl)(t-butylamido)M(R)₂; -   dimethylsilylene(6,6-diethyl-1,5,6,7-tetrahydro-s-indacen-1-yl)(t-butylamido)M(R)₂; -   dimethylsilylene(2-methyl-7,7-diethyl-3,6,7,8-tetrahydro-as-indacen-3-yl)(t-butylamido)M(R)₂; -   dimethylsilylene(7,7-diethyl-3,6,7,8-tetrahydro-as-indacen-3-yl)(t-butylamido)M(R)₂; -   dimethylsilylene(2-methyl-6,6-diethyl-1,5,6,7-tetrahydro-s-indacen-1-yl)(cyclododecylamido)M(R)₂; -   dimethylsilylene(6,6-diethyl-1,5,6,7-tetrahydro-s-indacen-1-yl)(cyclododecylamido)M(R)₂; -   dimethylsilylene(2-methyl-7,7-diethyl-3,6,7,8-tetrahydro-as-indacen-3-yl)(cyclododecylamido)M(R)₂; -   dimethylsilylene(7,7-dimethyl-3,6,7,8-tetrahydro-as-indacen-3-yl)(cyclododecylamido)M(R)₂; -   diethylsilylene(2,6,6-trimethyl-1,5,6,7-tetrahydro-s-indacen-1-yl)(t-butylamido)M(R)₂; -   diethylsilylene(6,6-dimethyl-1,5,6,7-tetrahydro-s-indacen-1-yl)(t-butylamido)M(R)₂; -   diethylsilylene(2,7,7-trimethyl-3,6,7,8-tetrahydro-as-indacen-3     -yl)(t-butylamido)M(R)₂; -   diethylsilylene(7,7-dimethyl-3,6,7,8-tetrahydro-as-indacen-3-yl)(t-butylamido)M(R)₂; -   dimethylsilylene(2-methyl-3,6,7,8-tetrahydro-as-indacen-3-yl)(cyclohexylamido)M(R)₂; -   dimethylsilylene(2-methyl-3,6,7,8-tetrahydro-as-indacen-3-yl)(cyclododecylamido)M(R)₂; -   dimethylsilylene(2-methyl-3,6,7,8-tetrahydro-as-indacen-3-yl)(adamantylamido)M(R)₂;     and -   dimethylsilylene(2-methyl-3,6,7,8-tetrahydro-as-indacen-3-yl)(t-butylamido)M(R)₂, -   where M is selected from Ti, Zr, and Hf and R is selected from     halogen or C₁ to C₅ alkyl, preferably R is a methyl group or a     halogen group, preferably M is Ti.

In alternative embodiments, a catalyst system can include two or more different transition metal compounds. For purposes of the present disclosure one transition metal compound is considered different from another if they differ by at least one atom. For example “Me₂Si(2,7,7-Me₃-3,6,7,8-tetrahydro-as-indacen-3-yl)(cyclohexylamido)TiCl₂” is different from Me2Si(2,7,7-Me3-3,6,7,8-tetrahydro-as-indacen-3-yl)(n-butylamido)TiCl₂” which is different from Me₂Si(2,7,7-Me₃-3,6,7,8-tetrahydro-as-indacen-3-yl)(n-butylamido)HfCl₂.

In some embodiments, formulae I to III are referred to as mono-tetrahydroindacenyl compounds, precatalysts and/or catalysts.

In at least one embodiment, one mono-tetrahydroindacenyl compound as described herein is used in the catalyst system.

The terms “cocatalyst” and “activator” are used herein interchangeably and include a compound which can activate any one of the catalyst compounds described above by converting the neutral catalyst compound to a catalytically active catalyst compound cation. Non-limiting activators, for example, include alumoxanes, aluminum alkyls, ionizing activators, which may be neutral or ionic, and conventional-type cocatalysts. Preferred activators typically include non-coordinating anion compounds, alumoxane compounds, modified alumoxane compounds, and ionizing anion precursor compounds that abstract a reactive, σ-bound, metal ligand making the metal complex cationic and providing a charge-balancing noncoordinating or weakly coordinating anion.

In some embodiments, the catalyst compounds described herein may be supported (with or without an activator) by any method effective to support other coordination catalyst systems, effective meaning that the catalyst so prepared can be used for oligomerizing or polymerizing olefin in a heterogeneous process. The catalyst precursor, activator, co-activator if needed, suitable solvent, and support may be added in any order or simultaneously. Typically, the complex and activator may be combined in solvent to form a solution. Then the support is added, and the mixture is stirred for 1 minute to 10 hours. The total solution volume may be greater than the pore volume of the support, but some embodiments limit the total solution volume below that needed to form a gel or slurry (about 90% to 400%, preferably about 100-200% of the pore volume). After stirring, the residual solvent is removed under vacuum, typically at ambient temperature and over 10-16 hours. But greater or lesser times and temperatures are possible.

The complex may also be supported absent the activator; in that case, the activator (and co-activator if needed) is added to a polymerization process's liquid phase. Additionally, two or more different complexes may be supported on the same support. Likewise, two or more activators or an activator and co-activator may be supported on the same support.

Suitable solid particle supports are typically comprised of polymeric or refractory oxide materials, each being preferably porous. A support material can have an average particle size greater than 10 μm for use in embodiments of the present disclosure. A support material can be a porous support material, such as, talc, inorganic oxides, inorganic chlorides, for example magnesium chloride and resinous support materials such as polystyrene polyolefin or polymeric compounds or any other organic support material and the like. A support material can be an inorganic oxide material including group-2, -3, -4, -5, -13, or -14 metal or metalloid oxides. A catalyst support materials can be silica, alumina, silica-alumina, and their mixtures. Other inorganic oxides may serve either alone or in combination with the silica, alumina, or silica-alumina. These are magnesia, titania, zirconia, and the like. Lewis acidic materials such as montmorillonite and similar clays may also serve as a support. In this case, the support can optionally double as the activator component, however, an additional activator may also be used.

For further details, see concurrently filed applications: 1) U.S. Ser. No. ______, entitled “Processes for Producing High Propylene Content PEDM using Tetrahydroindacenyl Catalyst Systems”, attorney docket number (2018EM053/2), which claims priority to and the benefit of U.S. Ser. No. 62/644,971, filed Mar. 19, 2018; and 2) U.S. Ser. No. ______, entitled “Processes for Producing High Propylene Content PEDM Having Low Glass Transition Temperatures Using Tetrahydroindacenyl Catalyst Systems”, attorney docket number (2018EM053A); which claims priority to and the benefit of U.S. Ser. No. 62/644,971, filed Mar. 19, 2018, which are incorporated by reference herein.

Preparing TPV Compositions

As those skilled in the art appreciate, dynamic vulcanization includes a process whereby a rubber that is undergoing mixing with a thermoplastic resin is cured (i.e., cross-linked, or vulcanized). The rubber is crosslinked or vulcanized under conditions of high shear at a temperature above the melting point of the thermoplastic resin. As a result of the process, the thermoplastic resin becomes the continuous phase of the mixture and the rubber becomes dispersed as a discontinuous phase within the continuous thermoplastic phase. Thus, in some embodiments, the mixture (e.g., the TPV formulation) undergoes a phase inversion during dynamic vulcanization, where the blend, which initially includes a major volume fraction of rubber, is converted to a blend where the plastic phase is the continuous phase and the rubber is simultaneously crosslinked and dispersed as fine particles within the thermoplastic matrix.

In general, the dynamic vulcanization of the TPV formulation takes place within a reactor, such as an extruder, melt-mixer, or other reactive mixing device (for example, a Banbury mixer or a Brabender mixer). An intermeshing twin-screw extruder is a preferred mixer. Furthermore, not all components of the TPV formulation need necessarily be introduced to the reactor at the same time. See, for example, U.S. Patent Publication 20170292016, hereby incorporated by reference in its entirety and for all purposes, which discloses addition of colorant and other additives both during and after the dynamic vulcanization process, as well as a “masterbatch” method of adding either or both of a curative formulation and a formulation of additional additives.

For instance, dynamic vulcanization can be performed as follows: The rubber component and thermoplastic component are mixed to form a blend, which may be referred to as a solids blend (although not all components of the blend need necessarily be in the solid state). Optional solid additives, such as cure accelerator, fillers, zinc oxide, and miscellaneous solids such as pigments and antioxidants, may be added to the solids blend. The blend is continually mixed at a temperature above the melt temperature of the thermoplastic resin to form a molten blend or “melt”. The vulcanizing agent (e.g., curative), which may be in the form of a solid or a liquid, is introduced to the molten blend to form a vulcanizable blend. Heating and mixing continues in order to effect dynamic vulcanization.

Processing oil can be introduced at any stage, or in multiple stages, of the process. For example, oil can be added to the solids blend, to the molten blend, together with the curative (e.g. as a resin-in-oil or “RIO” composition), or after dynamic vulcanization—or at any two or more of the foregoing points in the process. Processing oils are necessary for cooling the extruder to prevent viscous over-heating and to lower the viscosity in order to avoid extruder over-torque.

Methods according to particular embodiments include “preloading” process oil, meaning that a portion of the process oil is introduced to the TPV formulation before the curative is introduced. Surprisingly, it has been found that some degree of oil preloading may result in increased tensile properties of the resulting TPV, without increasing hardness, which may be desired in some foaming applications.

According to such embodiments, the preloaded oil (e.g., a first portion of process oil) is introduced into the molten blend of TPV formulation components before introducing the curative. Preferably, at least 15 wt %, more preferably at least 30 wt %, such as at least 40 wt %, or at least 50 wt %, of the total process oil used in forming the TPV is preloaded (i.e., introduced before the curative). In some embodiments, the amount of preloaded process oil is within the range from 15 to 60 wt %, such as 20 to 60 wt %, preferably 25 to 60 wt %, such as 25 to 55 wt %, 30 to 50 wt %, or 35 to 45 wt %, with ranges from any of the foregoing low ends to any of the foregoing high ends also contemplated in various embodiments. These weight percentage values are based on total weight of process oil added to the TPV (which is exclusive of any extender oil that may be present in the rubber component, but which includes process oil that might be added to the process with the curative, as is the case with phenolic resin-in-oil curatives).

Following dynamic vulcanization, mixing may continue and additional additives or ingredients can be incorporated into the molten product, which may be referred to as a molten thermoplastic vulcanizate. For example, post-vulcanization additives, such as acid scavengers (and additional process oil, as noted), can be added to the molten mass following dynamic vulcanization. The product can then be extruded through an extruder die, or otherwise fabricated, and ultimately cooled for handling and/or further processing. For example, the molten thermoplastic vulcanizate composition may be cooled and/or solidified and subsequently pelletized for future storage and/or shipment. Practice of embodiments of the present disclosure is not necessarily limited by the manner in which the thermoplastic vulcanizate composition is subsequently solidified or fabricated.

The process of dynamic vulcanization as described herein can take place in a continuous mixing reactor, which may also be referred to as a continuous mixer. Continuous mixing reactors may include those reactors that can be continuously fed ingredients and that can continuously have product removed therefrom. Examples of continuous mixing reactors include twin screw or multi-screw extruders (e.g., ring extruders). Methods and equipment for continuously preparing thermoplastic vulcanizates are described in U.S. Pat. Nos. 4,311,628; 4,594,390; 5,656,693; 6,147,160; and 6,042,260, as well as WO 2004/009327, which are incorporated herein by reference, although methods employing low shear rates can also be used. The temperature of the blend as it passes through the various barrel sections or locations of a continuous reactor can be varied as is known in the art. In particular, the temperature within the cure zone may be controlled or manipulated according to the half-life of the curative employed.

In the present disclosure, the thermoplastic component added to a formulation processed to prepare a TPV can be an isotactic polypropylene (iPP); the rubber component added the TPV formulation can be an EPDM rubber, and a PEDM terpolymer can be added to the TPV formulation as a compatibilizer; such TPV formulation can further include one or more diluents. A “diluent” is a non-reactive, non-curing component such as a mineral oil, naphthenic oil, linear or branched olefin oil, or some combination thereof. During mixing of such a TPV formulation, another portion of a diluent may be added (which may be the same or different from one included in the TPV formulation before such addition) and the mixing continued. Then one or more curatives or curative composition can be added, thus beginning the vulcanizing reactions and providing a reacting TPV formulation, and the mixing continued. A further portion of a diluent can be added and the mixing continued until the reacting is completed to a desired degree, providing a TPV composition, and then the TPV composition is recovered, for example by pressing the composition through an extrusion die at an appropriate temperature.

In some implementations of such a method as above, the EPDM rubber can be added in an amount from 35 to 55 wt % of the TPV formulation, isotactic polypropylene (iPP) can added in an amount from 20 to 30 wt % of the TPV formulation; the total amount of diluent added can be from 13 to 21 wt % of the TPV formulation, and a propylene-ethylene-diene terpolymer (PEDM) compatibilizer can be added in an amount from 0.5 to 15 wt % of the TPV formulation.

In some instances of such a method as above, the curative can be added as a resin-in-oil composition (such as a phenolic resin curative in oil), stannous chloride and/or zinc oxide. In such instances, typically the resin-in-oil composition is added to the mixing TPV formulation, and then after some further mixing, the stannous chloride and zinc oxide are added. The resin-in-oil composition can be added to a mixer in which the TPV formulation is reacting from a different physical location on the mixer from the position at which the zinc oxide and stannous chloride are added.

In some instances of a method as disclosed above, the mixing (and reacting, after the curative(s) are added) can be performed at a temperature of from 150 to 200° C. in a batch internal mixer, which can for example be a Brabender or Banbury mixer, running at from 80 to 120 rpm, and the mixing can be continued for about 1 minute between the step of mixing the iPP, EPDM, PEDM and first portion of diluent and the step of adding the second portion of diluent, and the mixing can be continued for about 2 minutes between the addition of the second portion of diluent and adding the curative(s), and the mixing can be continued for about 5 minutes between adding the curative(s) and the step of adding the third portion of diluent, and the mixing can then be continued for about 3 minutes before recovering the TPV composition.

Some instances of a method performed as disclosed above are performed at a temperature from 200 to 250° C. in a continuous twin-screw extruder running at from 50 to 200 RPM with 1 to 5 minutes of residence time of the TPV formulation. In some such implementations, the different components of the TPV formulation can be added from two or more different positions about the mixer. For example, the iPP, EPDM and PEDM components, with a first part of diluent might be added at a first position along the flow of a continuous intermeshing twin-screw extruder, and the second portion of diluent and the curative(s) might be added from a second position downstream from the first position.

Referring now to FIG. 2, a schematic illustration of one embodiment of a process and associated apparatus according to the present disclosure, a feed 1 comprising one or more of a polypropylene, e.g., iPP, a rubber component, e.g., an EPDM terpolymer, a compatibilizer e.g., a PEDM terpolymer and optional processing oil, is introduced to an internal mixer 3, e.g., an intermeshing twin-screw extruder, via an inlet 5 that is configured to receive the selected ingredients. The mixer is further configured with additional inlets for feeds for additional ingredients 7 a, 7 b, of the TPV formulation, e.g., one or more of a curative or another additive such as a filler. The mixer is further configured with one or more temperature controllers or heaters 9, configured to raise the temperature of the TPV composition to at least the Tm of the TPV composition and maintain the temperature of the TPV composition within the mixer, including at the inlet, along the length of the mixer and at the outlet 11, at a desired temperature between Tm and the degradation temperature of the TPV composition. The temperature need not be the same from the inlet along the length of the mixer and at the outlet, but can be varied along this path as desired. The melted TPV composition is mixed and reacted to form the thermoplastic vulcanizate and then fed via an outlet 11 to provide a TPV extrudate stream 13 that can be fed, for example, to a pelletizer (not shown) to be cooled and pelleted, or to any other desired downstream process. The outlet 11 can be configured with an extrusion die to shape the extrudate in some fashion if that is desired. The temperature of the outlet 11 is maintained at a desired temperature for extrusion or process for the recovery of the TPV composition by the temperature controller 9 configured to maintain the temperature of the TPV composition at the outlet.

For further information please refer to FIG. 3 of U.S. Ser. No. ______, filed concurrently herewith, entitled “Compatibilized Thermoplastic Vulcanizate Compositions”, attorney docket number (2018EM063/2) claims priority to and the benefit of U.S. Ser. No. 62/653,734 filed Apr. 6, 2018, which is incorporated by reference in its entirety, which is a process flow diagram for preparing TPV blends, at arrows 21, the basic ingredients of a TPV formulation (rubber component a, thermoplastic component “b”, oil “c”, compatibilizer “d” are introduced into a mixer and mixed to form a TPV formulation (i.e., an unvulcanized TPV composition) 23, which is subjected to further mixing at step 25 for a period of time. One or more curatives, or a curative composition comprising a vulcanizing agent and one or more curing accelerators “e” are mixed with the TPV formulation to form a reacting TPV formulation 27, which is subjected to further mixing 29. Further processing oil “f” is added to the partially or completely vulcanized composition 31 and mixing is continued to form a final TPV composition 35, which is then recovered and optionally can be further processed 37, e.g. by cooling and pelleting, or extrusion to form a slab or other shape 39.

Embodiments

Embodiment 1: A thermoplastic vulcanizate comprising an isotactic polypropylene matrix phase in which a cross-linked ethylene-propylene-diene terpolymer (EPDM) is dispersed, the vulcanizate being a reaction product of a mixture of:

a) 35 to 55 wt % of an ethylene-propylene-diene terpolymer (EPDM);

b) 10 to 40 wt % of isotactic polypropylene (iPP);

c) 0.5 to 25 wt % of a propylene-ethylene-diene terpolymer (PEDM) compatibilizer (preferably having a heat of fusion of less than 2 J/g); and

d) 0.015 to 0.03 wt % of curatives;

wherein the percentages of components (a) to (d) are based on the total weight of the mixture.

Embodiment 2: The thermoplastic vulcanizate of embodiment 1, further comprising at least 10 wt % of a diluent.

Embodiment 3: The thermoplastic vulcanizate of embodiment 1 or 2, in which the the EPDM comprises 55 to 75 wt % ethylene, 2 to 10 wt % 5-ethylidene-2-norbornene and 43 to 15 wt % propylene.

Embodiment 4: The thermoplastic vulcanizate of any one of embodiments 1 to 3, in which the amount of PEDM is present at from 2 to 30 wt % of the amount of EPDM.

Embodiment 5: The thermoplastic vulcanizate of any one of embodiments 1 to 4, in which the PEDM has viscosity of MST (5+4) @ 230C is from 5 to 90.

Embodiment 6: The thermoplastic vulcanizate of any one of embodiments 1 to 5, in which the PEDM comprises 5 to 18 wt % ethylene and 2 to 12 wt % 5-ethylidene-2-norbornene.

Embodiment 7: The thermoplastic vulcanizate of any one of embodiments 1 to 6, in which the particle size dispersity index (PSDI) of the rubber particles is less than 3.

Embodiment 8: The thermoplastic vulcanizate of any one of embodiments 1 to 7, in which the thermoplastic vulcanizate further comprises clay and carbon black.

Embodiment 9: The thermoplastic vulcanizate of any one of embodiments 1 to 8, in which the PEDM has a heat of fusion (Hf) which is greater than or equal to 0 and less than or equal to 5 J/g.

Embodiment 10: The thermoplastic vulcanizate of any one of embodiments 1 to 8, in which the PEDM has a heat of fusion (Hf) which is greater than or equal to 0 and less than or equal to 2 J/g.

Embodiment 11. A TPV composition made by such a method comprising (or consisting of, or consisting essentially of):

i) mixing an iPP, EPDM, and PEDM, and a diluent to prepare a TPV formulation;

ii) adding one or more curatives to the TPV formulation and continuing mixing to perform dynamic vulcanization; and

iii) recovering the TPV composition.

Embodiment 12. The method of embodiment 11, further comprising adding a diluent to the TPV formulation prior to step ii) and continuing mixing.

Embodiment 13. The method of embodiment 12, further comprising adding a further portion of diluent following step ii) and continuing mixing and dynamic vulcanization to form a TPV composition.

Embodiment 14: The method of any one of embodiments 11 to 13, wherein the curatives are a phenolic resin in oil composition, stannous chloride and zinc oxide.

Embodiment 15: The method of any one of embodiments 11 to 14, wherein the ethylene-propylene-diene terpolymer (EPDM) is added in an amount from 35-55 wt % of the TPV formulation, the isotactic polypropylene (iPP) is added in an amount from 10 to 40 wt % of the TPV formulation; diluent is added in an amount from 13 to 21 wt % of the TPV formulation, a propylene-ethylene-diene terpolymer (PEDM) compatibilizer is added in an amount from 0.5-15 wt % of the TPV formulation.

Embodiment 16: The method of any one of embodiments 11 to 15, wherein the method is performed at a temperature of from 150 to 200° C. in an internal mixer running at from 80 to 120 rpm and mixing continues for about 1 minute prior to step ii), for about 2 minutes after the first addition of diluent, for about 5 minutes after the second addition of diluent and for about 3 minutes after step iii).

Embodiment 17: The method of any one of embodiments 11 to 15, wherein the method is performed at a temperature from 200 to 250° C. in a continuous twin-screw extruder running at from 50 to 200 RPM with 1 to 5 minutes of residence time wherein the iPP, EPDM, and PEDM, and first portion of a diluent are added to the extruder at a first position of the extruder, and at least one of the second portion of diluent, the curatives and the third portion of diluent are added to the extruder at least a second position downstream from the first position.

Embodiment 18: The method of any one of embodiments 11 to 17, wherein the method is performed at a temperature of from 150 to 200° C. in an internal mixer running at from 80 to 120 rpm and mixing continues for about 1 minute after step i), for about 2 minutes after the first addition of diluent, for about 5 minutes after the second addition of diluent and for about 3 minutes after step iii); and then mixing is performed for about 1 to 5 additional minutes.

Embodiment 19: The method of any one of embodiments 11 to 18, wherein the method is performed at a temperature from 200 to 250° C. in a continuous twin-screw extruder running at from 50 to 200 RPM with 1 to 5 minutes of residence time; and in which the RIO composition is added to the extruder at a first position, followed by additional mixing.

Embodiment 20: The method of any one of embodiments 11 to 18, wherein the PEDM has a heat of fusion (Hf) which is greater than or equal to 0 and less than or equal to 2 J/g.

Embodiment 21: The method of any one of embodiments 1 to 19 wherein the thermoplastic vulcanizate has a Dw/Dn of 7 or less.

Embodiment 22: The method of any one of embodiments 1 to 19, wherein the thermoplastic vulcanizate has a tension set at 50% elongation of 14% or less.

Embodiment 23: The method of any one of embodiments 1 to 19, wherein the thermoplastic vulcanizate has a tension set at 50% elongation of 14% or less and a Dw/Dn of 7 or less.

Embodiment 24:The method of any one of embodiments 1 to 23, wherein the thermoplastic vulcanizate has an elongation at break of 200% or more, alternately 225% or more, alternately 250% or more, as determined by the method described below.

Embodiment 24:The method of any one of embodiments 1 to 24, wherein the thermoplastic vulcanizate has a break stress of 4 MPa or more, alternately 5 MPa or more, as determined by the method described below.

Embodiment 25:The method of any one of embodiments 1 to 24, wherein the thermoplastic vulcanizate has a tension set from 25% elongation of 7% or less, alternately 6% or less, alternately 5% or less, as determined by the method described below.

Embodiment 26: The method of any one of embodiments 1 to 25, wherein the thermoplastic vulcanizate has an number average particle size diameter of the rubber particles (PEDM and EPDM) of 800 nm or less, alternately 700 nm or less, alternately 600 nm or less, as determined by the method described below.

Embodiment 27: The method of any one of embodiments 1 to 26, wherein the thermoplastic vulcanizate has has a dispersity of crosslinked particle size diameter of the rubber particles (PEDM and EPDM) of 1.6 or less, alternately 1.5 or less, alternately 1.4 or less, or 1.3 or less, as determined by the method described below.

Embodiment 28: The method of any one of embodiments 1 to 27 wherein the thermoplastic vulcanizate has:

1) a Dw/Dn of 7 or less;

2) a tension set at 50% elongation of 14% or less;

3) an elongation at break of 200% or more, alternately 225% or more, alternately 250% or more;

4) a break stress of 4 MPa or more, alternately 5 MPa or more, as determined by the method described below;

5) a tension set from 25% elongation of 7% or less, alternately 6% or less, alternately 5% or less;

6) a number average particle size diameter of the rubber particles of 800 nm or less, alternately 700 nm or less, alternately 600 nm or less;

7) a dispersity of crosslinked particle size diameter of the rubber particles of 1.6 or less, alternately 1.5 or less, alternately 1.4 or less, or 1.3 or less.

Experimental

Z-average (Mz), weight-average (Mw), number average molecular weights (Mn), viscosity average (Mv) molecular weights and the molecular weight of the highest peak (Mp) can be measured using gel permeation chromatography (GPC), also known as size exclusion chromatography (SEC). This technique utilizes an instrument containing columns packed with porous beads, an elution solvent, and detector in order to separate polymer molecules of different sizes. In a typical measurement, the GPC instrument used is a Waters chromatograph equipped with ultrastyro gel columns operated at 145° C. The elution solvent used is trichlorobenzene. The columns are calibrated using sixteen polystyrene standards of precisely known molecular weights. A correlation of polystyrene retention volume obtained from the standards, to the retention volume of the polymer tested yields the polymer molecular weight.

Average molecular weights M (Mw, Mn, Mz) can be computed from known expressions. The desired MWD function (e.g., Mw/Mn or Mz/Mw) is the ratio of the corresponding M values. Measurement of M and MWD are well known in the art and are discussed in more detail in, for example, Slade, P. E. Ed., Polymer Molecular Weights Part II, Marcel Dekker, Inc., N.Y., (1975) 287-368; Rodriguez, F., Principles of Polymer Systems 3rd Ed., Hemisphere Pub. Corp., NY, (1989) 155-160; U.S. Pat. No. 4,540,753; Ver Strate et al., Macromolecules, Vol. 21, (1988) pp. 3360-3371, each of which is incorporated herein by reference.

All TPV samples, including control examples, were cryo-faced using a cryo-microtom (Leica) and examined afterward by a tapping phase AFM (atomic force microscopy, Icon, Bruker). For each sample, three 60 by 60 micron phase images were collected and then processed by SPIP software (scanning probe image processing, Image Metrology). Image processing results of all examples are tabulated in Tables below along with their mechanical properties. Particle count is the number of dispersion particles measured in images and Dn, Dw, and Dv are equivalent dispersion diameters of number average, weight average, and volume average respectively. Dw/Dn is the “particle size dispersity index”, or PSDI, and is a measure of the size dispersity. The area percent is the percentage of area occupied by these vulcanized rubber particles.

Mooney viscosity: Mooney Small Thin viscosity (MST) (5+4) at 230° C. and Mooney Small Thin relaxation area (MSTRA) are determined using ASTM D1646.

All TPV samples were compression molded into test specimens for mechanical measurements.

Flexural modulus was determined according to ASTM D-790 ProA, at 0.05 in/min deformation rate, in MPa.

Hysteresis values were determined by the energy loss, in J, during tensile extensions to 200% in 2 cycles at 200 mm/min. The 1^(st) hysteresis is for the 1^(st) cycle of loading and unloading and 2^(nd) hysteresis is for the 2^(nd) cycle of loading and unloading. Hysteresis values are determined using the method described at U.S. Pat. No. 9,938,400, Column 31, line 63 to column 32, line 44.

Tension set was determined according to ASTM D-412 Method A using a dumbbell shaped die cut sample at room temperature. 25% and 50% extension of the sample was used with the elongation and relaxation times as specified with elongation speed of 50mm/min being used.

Tensile strength, % strain and strain property values were obtained from samples tested according to ASTM D638, except that the separation of the grips (30 mm grip) was conducted at 50.8 cm/min (20 in/min). The extension of the grips and thus the samples was independently determined using an extensometer attached to the testing apparatus. The tensile strength data were reported in engineering units (MPa or psi), and the elongation was reported as the % elongation of the distension zone of the sample.

Dynamic Mechanical Thermal Analysis (DMTA): Dynamic mechanical thermal analysis (DMTA). This test provides information about the small-strain mechanical response (relaxation behavior) of a sample as a function of temperature over a temperature range that includes the glass transition region and the visco-elastic region prior to melting.

Typically, samples were tested using a three point bending configuration (TA Instruments DMA 2980). A solid rectangular compression molded bar was placed on two fixed supports; a movable clamp applied a periodic deformation to the sample midpoint at a frequency of 1 Hz and amplitude of 20 μm. The sample was initially cooled to −130° C. then heated to 60° C. at a heating rate of 3° C./min. In some cases, compression molded bars were tested using other deformation configurations, namely dual cantilever bending and tensile elongation (Rheometrics RSAII). The periodic deformation under these configurations was applied at a frequency of 1 Hz and strain amplitude of 0.05%. The sample was cooled to −130° C. and then heated to 60° C. at a rate of 2° C./min. The slightly difference in heating rate does not influence the glass transition temperature measurements significantly.

Shore A Hardness: The determination of the Shore A hardness is according to ASTM D 2240. In this version of the method a portion of the sample is tested at room temperature. The data is recorded 15 seconds after the indentation is created in the sample.

MFR was determined according to ASTM D 1238 (2.16kg, 230° C.).

Materials:

Resin-in-oil, RIO, curative composition is 30/70 resin/oil composition containing paraffinic oil and a phenolic resin (SP1045™ phenolic (octylphenol-formaldehyde resin with methylol active group), or HRJ16261™ phenolic resin, both obtained from Schnedtady Chemical Inc., SI Group).

PP5341™—isotactic polypropylene, iPP, having a melt flow rate, MFR, of 0.8 dg/min, available from ExxonMobil Chemical Company.

Irganox™ 1076—hindered phenolic antioxidant available from Ciba-Geigy.

Irgafos™ 168—phosphite antioxidant available from Ciba-Geigy.

AMP™ 49974—carbon black masterbatch, obtained from Ampecet Corporation.

IcecapK™—clay available from Burgess Pigment Company.

Paralux™ 6001R—water white paraffinic process oil available from Chevron Texaco.

ParaMount™ 6001R—paraffinic process oil available from Chevron Texaco.

Sunpar™ 150—paraffinic oil available from R. E. Carroll, Inc.

Vistalon™ 3666 EPDM, —oil extended (75phr) ethylene propylene diene momomer rubber having 65 wt % ethylene, 4.5% ENB, and having a 52 Mooney, available from ExxonMobil Chemical Company.

Keltan™ 597Q—EPDM oil extended (100 phr oil) EPDM having 62% ethylene, 4.0% ENB, 55 Mooney, available from Arlanxeo Company.

EXAMPLES

The following examples are presented for illustrative purposes and not intended to limit the scope of the present disclosure.

Example 1 PEDM Synthesis (PEDM-1, PEDM-2, PEDM-3, PEDM-4)

PEDMs were produced using a solution process in a 0.5-liter continuous stirred-tank reactor (autoclave reactor). The autoclave reactor was equipped with a stirrer, a water-cooling/steam-heating element with a temperature controller, and a pressure controller. Solvents and monomers were first purified by passing through a three-column purification system. The purification system consisted of an Oxiclear column (Model #RGP-R1-500 from Labclear) followed by a 5A and a 3A molecular sieve column. Purification columns were regenerated periodically whenever there was evidence of low catalyst activity. Isohexane was used as a solvent. Solvent was fed into the reactor using a Pulsa pump and its flow rate was controlled by adjusting the outflow at the pump (using a calibration curve). The compressed, liquefied propylene feed was controlled by a mass flow controller. Ethylene was mixed with propylene before the reactor and fed to a reactant inlet manifold. A mixture of isohexane and tri-n-octylaluminum (TNOAL) and ethylene norbornene (ENB) was also added to the reactant inlet manifold through a separate line and the combined mixture of monomers and solvent was fed into the reactor using a single tube.

The polymerization catalyst used was bis(p-triethylsilylphenyl) carbyl(cyclopentadienyl) (2,7-di-t-butylfluorenyl) hafnium dimethyl activated by N,N-dimethylanilinium tetrakis(pentafluorophenyl) borate. Both the catalyst and activator were first dissolved in toluene and the solutions were kept in an inert atmosphere. The solutions of catalyst and activator were premixed and fed into the reactor using an ISCO syringe pump. The catalyst to activator feed ratio (molar) was set at 0.98. The collected samples were first placed on a boiling-water steam table in a hood to evaporate a large fraction of the solvent and unreacted monomers, and then dried in a vacuum oven at a temperature of ˜90° C. for 12-18 hours. The vacuum oven dried samples were weighed to obtain yields. All reactions were carried out at a gauge pressure of about 2.2 MPa and at temperatures from 100 to 120° C. Compositions of these amorphous PEDMs (with zero crystallinity) thus prepared are shown in Table 1, where the “wt %” ethylene is the weight percent of ethylene-derived units by weight of the PEDM, and the wt % ENB is the weight percent of the ethylene-norbornene-derived units by weight of the PEDM. MFR was measured at 230° C. at 2.16 kg loading.

TABLE 1 PEDM compatibilizers synthesized. Ethylene ENB MFR, Δ Hf by DSC (wt %) (wt %) g/10 min J/g PEDM1 15 2.9 16 <0.25 PEDM2 11.4 2.8 1.0 <0.25 PEDM3 16.5 11.3 3.3 <0.25 PEDM4 12 3.6 1.1 <0.25

TPV Preparation

The main ingredients used in the exemplary TPVs are isotactic polypropylene (iPP) (PP5341™, 0.8 MFR, ExxonMobil Chemical), EPDM (oil extended with 75 phr oil, 64% ethylene, 4.5% ENB, 52 Mooney, ExxonMobil Chemical Company), and oil (Sunpar™ 150). Curatives employed for vulcanization included phenolic resin in oil (RIO), stannous chloride, SnCl₂, and zinc oxide, ZnO. The RIO composition is 30/70 resin/oil composition (here a paraffinic oil, Sunpar™ 150) the resin used is SP1045™ phenolic (octylphenol-formaldehyde resin with methylol active group). Detailed TPV formulations for Examples 1 to 25 are found in Tables 2 to 5 below. Amounts are in grams. It should be noted that oil amount is adjusted in each formulation according to the EPDM amount used since the EPDM used contains oil by itself. The adjustment ensures that the final and total oil amount in each formulation is the same. The amounts of PEDM used are from 0.4, 0.9, 1.9, 2.8, 3.8, to 5.6 gm, corresponding to 2 wt %, 5 wt %, 10 wt %, 15 wt %, 20 wt %, and 30 wt % of PEDM to EPDM. All TPVs were prepared in a Brabender internal mixer running at 180° C. (356° F.) and 100 RPM. EPDM, PEDM, and PP were added at the beginning, after 1 minute, ½ of the oil was added, then after 2 min, the RIO was introduced, mixed for 1 min and SnCl₂/ZnO was added, mixed for another 5 min, finally the other ½ of oil was added and mixed for 3 minutes. The total mix time was 12 minutes.

TABLE 2 TPV Compound Formulations without PEDM and with PEDM1. Example 1 Example 2 Example 3 Example 4 Example 5 Example 6 Example 7 EPDM 32.8 32.2 31.2 29.5 27.9 26.3 23.0 PP 18.8 18.8 18.8 18.8 18.8 18.8 18.8 Oil 8.44 8.72 9.14 9.84 10.55 11.25 12.66 PEDM1 0.0 0.4 0.9 1.9 2.8 3.8 5.6 Curatives: RIO 0.9 0.9 0.9 0.9 0.9 0.9 0.9 SnCl₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 ZnO 0.4 0.4 0.4 0.4 0.4 0.4 0.4

TABLE 3 TPV Compound Formulations Containing PEDM2. Example 8 Example 9 Example 10 Example 11 Example 12 Example 13 EPDM 32.2 31.2 29.5 27.9 26.3 23.0 PP 18.8 18.8 18.8 18.8 18.8 18.8 Oil 8.72 9.14 9.84 10.55 11.25 12.66 PEDM2 0.4 0.9 1.9 2.8 3.8 5.6 Curatives: RIO 0.9 0.9 0.9 0.9 0.9 0.9 SnCl₂ 0.1 0.1 0.1 0.1 0.1 0.1 ZnO 0.4 0.4 0.4 0.4 0.4 0.4

TABLE 4 TPV Compound Formulations Containing PEDM3. Example Example Exam- Exam- Exam- Exam- 14 15 ple 16 ple 17 ple 18 ple 19 EPDM 32.2 31.2 29.5 27.9 26.3 23.0 PP 18.8 18.8 18.8 18.8 18.8 18.8 Oil 8.72 9.14 9.84 10.55 11.25 12.66 PEDM3 0.4 0.9 1.9 2.8 3.8 5.6 Curatives: RIO 0.9 0.9 0.9 0.9 0.9 0.9 SnCl₂ 0.1 0.1 0.1 0.1 0.1 0.1 ZnO 0.4 0.4 0.4 0.4 0.4 0.4

TABLE 5 TPV Compound Formulations Containing PEDM4. Example Example Exam- Exam- Exam- Exam- 20 21 ple 22 ple 23 ple 24 ple 25 EPDM 32.2 31.2 29.5 27.9 26.3 23.0 PP 18.8 18.8 18.8 18.8 18.8 18.8 Oil 8.72 9.14 9.84 10.55 11.25 12.66 PEDM3 0.4 0.9 1.9 2.8 3.8 5.6 Curatives: RIO 0.9 0.9 0.9 0.9 0.9 0.9 SnCl₂ 0.1 0.1 0.1 0.1 0.1 0.1 ZnO 0.4 0.4 0.4 0.4 0.4 0.4

TABLE 6 TPV Compound Properties and Dispersion Sizes (containing PEDM1). Example 1 Example 2 Example 3 Example 4 Example 5 Example 6 Example 7 Break stress (MPa) 4.16 4.46 4.01 4.25 3.75 3.88 3.96 Break strain (%) 134.5 188.08 131.21 163.83 76.84 153.56 169.73 Flex modulus (MPa) 72.73 73.21 71.16 66.58 63.54 62.63 57.94 1^(st) hysteresis (Joules) 0.707 0.979 0.501 0.773 0.337 0.627 0.678 2^(nd) Hysteresis (Joules) 0.021 0.2 0.019 0.023 0.021 0 0 Dispersion: Dn (nm) 464.7 1128.0 535.9 678.1 422.1 534.0 554.3 Dw (nm) 3614.1 3143.5 2578.8 2119.5 2435.4 1935.9 1890.4 Dv (nm) 10805.3 6052.6 6879.8 4299.1 8667.3 4181.4 3877.5 Dw/Dn 7.8 2.8 4.8 3.1 5.8 3.6 3.4 Area % 61.2 56.8 55.2 54.7 52.7 59.3 58.7 Count 5019 2206 5508 5249 7074 7910 7734

TABLE 7 TPV Compound Properties and Dispersion Sizes (containing PEDM2). Example 8 Example 9 Example 10 Example 11 Example 12 Example 13 Break stress (MPa) 4.12 4.38 4.22 4.2 3.72 4.26 Break strain (%) 171.67 230.02 205.84 204.06 151.93 225.03 Flex modulus (MPa) 107.25 115.83 99.43 103.1 85.56 87.49 1^(st) hysteresis 0.981 1.070 1.027 1.138 0.631 1.074 (Joules) 2^(nd) 0.126 0.340 0.264 0.471 0.004 0.444 Hysteresis (Joules) Dispersion: Dn (nm) 1297.2 1037.0 841.7 570.2 549.2 630.6 Dw (nm) 3353.0 2671.0 3137.0 2238.7 2157.5 2134.1 Dv (nm) 6426.3 5113.1 10176.8 5254.7 6137.8 5238.0 Dw/Dn 2.6 2.6 3.7 3.9 3.9 3.4 Area % 52.45 48.55 58.51 53.87 51.1 52.91 Count 1662 2419 3054 5818 5947 5421

TABLE 8 TPV Compound Properties and Dispersion Sizes (containing PEDM3). Example 14 Example 15 Example 16 Example 17 Example 18 Example 19 Break stress (MPa) 4.71 4.69 3.86 5.07 5.87 5.65 Break strain (%) 240.29 250.56 129.34 294.31 351.29 379.67 Flex modulus (MPa) 102.43 89.67 80.47 93.89 80.14 84.52 1^(st) hysteresis 1.057 1.124 0.618 1.058 1.168 1.121 (Joules) 2^(nd) Hysteresis 0.382 0.472 0.006 0.391 0.520 0.401 (Joules) Dispersion: Dn (nm) 538.3 948.6 467.8 757.7 1057.1 998.9 Dw (nm) 3248.8 3600.3 3140.6 2672.5 2140.3 1892.6 Dv (nm) 11131.6 10929.3 10874.8 8940.7 2846.0 2484.7 Dw/Dn 6.0 3.8 6.7 3.5 2.0 1.9 Area % 58.41 58.48 59.13 58.22 58.99 53.88 Count 4604 2360 5548 3964 3601 3939

TABLE 9 TPV Compound Properties and Dispersion Sizes (containing PEDM4). Example Example Example Example Example Example 20 21 22 23 24 25 Break stress 6.51 6.29 5.45 5.48 5.47 4.96 (MPa) Break strain (%) 417.64 384.23 375.26 363.4 299.53 283.8 Flex modulus 80.96 90.55 90.36 103.84 97.68 100.25 (MPa) 1^(st) hysteresis 1.133 1.156 1.132 1.181 1.205 0.876 (Joules) 2^(nd) 0.503 0.514 0.470 0.495 0.525 0.287 Hysteresis (Joules) Dispersion: Dn (nm) 1185.5 1002.9 1089.7 886.4 848.7 777.9 Dw (nm) 2525.2 1981.5 1936.0 1818.5 1689.5 1721.1 Dv (nm) 4005.3 2991.5 2500.4 2689.2 2524.5 2823.2 Dw/Dn 2.1 2.0 1.8 2.1 2.0 2.2 Area % 56.43 57.87 57.6 53 51.5 54.63 Count 2604 4021 3766 4547 4959 5637

PEDM Compatibilizer Effects

The addition of PEDM, preferably PEDM2, into a PE/EPDM TPV can lower the dispersion size and improve the dispersion uniformity. The reductions in weight average dispersion size and particle size dispersity index (PSDI=Dw/Dn), in these TPVs is found with the addition of PEDM. Reducing PSDI contributes to enhancements in toughness by raising the elongation to break and break stress. Hence, the addition of PEDM compatibilizer in a PP/EPDM TPV lowers the EPDM dispersion size, improves EPDM dispersion uniformity, and raises the TPV toughness.

Example 2 For Ease of Reference, Data in Example 2 is Reproduced From U.S. Ser. No. ______, Filed Concurrently Herewith, Entitled “Thermoplastic Vulcanizates and Compositions Therefrom”, Attorney Docket Number (2019EM081). PEDM Synthesis for Formulation One

PEDMs were produced using a solution process in a 0.5-liter continuous stirred-tank reactor (autoclave reactor). The autoclave reactor was equipped with a stirrer, a water-cooling/steam-heating element with a temperature controller, and a pressure controller. Solvents and monomers were first purified by passing through a three-column purification system. The purification system consisted of an Oxiclear column (Model #RGP-R1-500 from Labclear) followed by a 5A and a 3A molecular sieve column. Purification columns were regenerated periodically whenever there was evidence of low catalyst activity. Isohexane was used as a solvent. Solvent was fed into the reactor using a Pulsa pump and its flow rate was controlled by adjusting the outflow at the pump (using a calibration curve). The compressed, liquefied propylene feed was controlled by a mass flow controller. Ethylene was mixed with propylene before the reactor and fed to a reactant inlet manifold. A mixture of isohexane and tri-n-octylaluminum (TNOAL) and ethylene norbornene (ENB) was also added to the reactant inlet manifold through a separate line and the combined mixture of monomers and solvent was fed into the reactor using a single tube. Tri-n-octylaluminum (TNOAL, available from Sigma Aldrich, Milwaukee, Wis.) solution was diluted to a concentration of 1.843×10-6 using isohexane.

Isohexane and TNOAL solutions were fed using Pulsa pumps and their flow rate was controlled using a pump calibration curve. Purified propylene, and ENB were also fed using Pulsa pumps but their flow rate was controlled using mass-flow controllers. The feed rate of purified ethylene was also regulated using a mass flow controller. Ethylene and propylene combined into a single line before entering a manifold upstream of the reactor. Isohexane, TNOAL solution, and ENB solution lines also combined in a single line before entering the same manifold. The resulting two lines merged further downstream and the combined mixture of monomers and solvent was fed into the reactor using a single tube.

Catalyst used in these examples was bis(p-triethylsilylphenyl)carbyl(cyclopentadienyl)(2,7-di-t-butylfluorenyehafniumdimethyl (Catalyst 1) and the activator used was dimethylaniliniumtetrakis(heptafluoronaphthyl)borate (Activator 1). The catalyst/activator solution was prepared daily and used on the same day. The solution was prepared by dissolving 80 mg of the catalyst and 99.1 mg of the activator in 450 ml toluene (catalyst concentration=1.884×10-07 mol/ml, catalyst/activator (molar ratio)=0.98). This solution was pumped into the reactor through a designated dip-tube at a desired rate using an Isco pump.

Composition was controlled by adjusting the feed ratio of the monomers while the molecular weight of the polymer, under fixed feed conditions, was controlled using temperature. The collected samples were first placed on a boiling-water steam table in a hood to evaporate a large fraction of the solvent and unreacted monomers, and then, dried in a vacuum oven at a temperature of about 90° C. for about 12 hours. The vacuum oven dried samples were weighed to obtain yields. The ethylene and ENB content of the polymer was determined by Fourier-transform infrared spectroscopy (FTIR). The monomer conversions were calculated using the polymer yield, composition and the amount of monomers fed into the reactor. Catalyst activity (also referred as to catalyst productivity) was calculated based the yield and the feed rate of catalyst. All the reactions were carried out at a gauge pressure of about 2.2 MPa. MST (Mooney Small Thin) measurements were made as a proxy for molecular weight. Polymers were made according to the conditions described in Table 1A. Characterization data are reported in Table 2A.

TABLE 1A PEDM Polymers Rxr Ethylene Propylene ENB Catalyst 1 Activator 1 Scavenger Isohexane Toluene Temp Feed Feed Feed Feed Feed Feed Feed Feed Sample (° C.) (g/min) (g/min) (mol/min) (mol/min) (mol/min) (g/min) (g/min) (g/min) 1 100 3 5 0.22 1.884E−07 1.922E−07 7.37E−06 81.7 0.866 2 100 3 4.5 0.22 1.884E−07 1.922E−07 7.37E−06 81.7 0.866 3 100 3 4.5 0.22 2.355E−07 2.403E−07 7.37E−06 81.7 1.0825 4 100 4 6 0.36 1.884E−07 1.922E−07 7.37E−06 81.8 0.866 5 100 4 5 0.36 1.884E−07 1.922E−07 7.37E−06 81.8 0.866 6 100 4 4 0.36 1.884E−07 1.922E−07 7.37E−06 81.8 0.866 7 100 4 4 0.36 2.825E−07 2.883E−07 7.37E−06 81.8 1.299 8 100 4 4 0.36 3.767E−07 3.844E−07 7.37E−06 81.8 1.732 9 100 4.25 4 0.36 3.767E−07 3.844E−07 7.37E−06 81.8 1.732 10 100 4.25 3.5 0.36 5.651E−07 5.766E−07 7.37E−06 81.8 2.598 11 100 4 6 0.45 1.884E−07 1.922E−07 7.37E−06 81.8 0.866 12 100 3 7 0.45 1.884E−07 1.922E−07 7.37E−06 81.8 0.866 13 100 2 8 0.45 2.355E−07 2.403E−07 7.37E−06 81.8 1.0825 14 100 1 9 0.36 3.767E−07 3.844E−07 7.37E−06 81.8 1.732 15 100 2 8 0.40 1.884E−07 1.922E−07 7.37E−06 81.8 0.866 16 100 2 8 0.40 9.418E−08 9.610E−08 7.37E−06 81.8 0.433 17 90 2 8 0.40 2.355E−07 2.403E−07 7.37E−06 81.8 1.0825 18 90 2 8 0.40 1.413E−07 1.442E−07 7.37E−06 81.8 0.6495 19 80 2 8 0.40 1.884E−07 1.922E−07 7.37E−06 81.8 0.866 20 80 2 8 0.40 2.825E−07 2.883E−07 7.37E−06 81.8 1.299 21 80 1 9 0.45 3.767E−07 3.844E−07 7.37E−06 81.8 1.732 22 80 1 9 0.45 3.767E−07 3.844E−07 7.37E−06 81.8 1.732 23 80 2 8 0.40 9.418E−08 9.610E−08 7.37E−06 81.8 0.433 24 90 3 7 0.45 1.884E−07 1.922E−07 7.37E−06 81.8 0.866 25 80 3 7 0.45 1.884E−07 1.922E−07 7.37E−06 81.8 0.866 26 80 1 9 0.40 1.884E−07 1.922E−07 7.37E−06 81.8 0.866

TABLE 2A Characterization of PEDM polymers produced in Table 1A C2 (wt %) Mooney MST Sample Sample uncorrected ENB (wt %) (5 + 4) @200 C. quantity (g) 1 46.1% 2.3% 34.4 70.1 2 47.9% 2.2% 37 70.2 3 46.4% 1.9% 28.6 78.6 4 49.6% 2.4% 41.4 141.6 5 53.4% 2.8% 51.1 132.1 6 57.5% 3.2% 61.4 122.8 7 56.4% 3.1% 40.8 199.1 8 53.1% 3.0% 30.4 157.5 9 55.2% 3.0% 34.6 322.6 10 50.2% 3.1% 24.6 340.2 11 56.5% 3.2% 48.7 263.1 12 41.4% 3.4% 33.7 257.2 13 31.0% 3.4% 17.5 218.3 14 18.8% 2.5% 17.4 47.7 15 32.8% 2.9% 21 198.3 16 35.2% 2.8% 28.6 190.8 17 30.4% 3.0% 32.8 175.4 18 31.6% 2.8% 42.5 124.3 19 30.4% 2.9% 46.2 159.7 20 28.4% 3.2% 41.7 216.4 21 16.1% 4.0% 29.9 228.4 22 33.0% 2.8% 59.8 161.1 23 40.2% 2.8% 44.1 305.8 24 38.5% 2.7% 60.6 238 25 14.1% 0.1% 36.5 401.8

Aggregation of PEDM Samples

Sixteen samples were then prepared from the above individual samples. Some samples were aggregated with others. The sixteen samples and characterization data are reported in Table 3A.

TABLE 3A Aggregated PEDM samples Mooney C2 (wt %) uncorrected ENB (wt %) MST (5 + 4) @200 C. 3-1 47.0% 2.3% 35.5 3-2 49.6% 2.4% 41.4 3-3 53.4% 2.8% 51.1 3-4 56.4% 3.1% 40.8 3-5 53.1% 3.0% 30.4 3-6 55.2% 3.0% 34.6 3-7 50.2% 3.1% 24.6 3-8 56.5% 3.2% 48.7 3-9 41.4% 3.4% 33.7 3-10 32.0% 3.1% 19 3-11 35.20%  2.82%  28.6 3-12 30.40%  2.98%  32.8 3-13 31.00%  2.85%  44.3 3-14 28.38%  3.16%  41.7 3-15 32.98%  2.80%  59.8 3-16 38.25%  2.68%  60.6

Formulation of TPV'S

The above aggregated samples in Table 3 were converted to TPV's of Formulation One in two compositions—Formulation One Recipe One and Formulation One Recipe Two (see Table 4A) as follows:

TABLE 4A TPV's of Formulation One PEDM by PP by Plasticizer by weight weight weight Sunpar ™ 150 Formulation One Recipe One 100 60 80 Formulation One Recipe Two 100 100 120

Step One: Preparation of Masterbatch

Samples 3-1 to 3-16 were converted to an intermediate masterbatch containing 28 grams isotactic polypropylene (iPP, PP5341™, 0.8 MFR, ExxonMobil Chemical Company); 141 grams PEDM from Table 3A; 42 grams plasticizer oil (SunparTM 150); 160 mg Irganox™ 1076; and 168 mg Irgafos™ 168. The blends were mixed for 5 minutes at 200 ° C. in a Brabender internal mixer. These masterbatch samples are numbered 5-1 to 5-16 corresponding to the samples in Table 3A, 3-1 to 3-16.

Masterbatch samples 5-1 to 5-16 were then converted to two TPV's, according to Formulation One Recipes One and Two.

TPV Preparation

The curatives employed for vulcanization included phenolic resin in oil, RIO, stannous chloride, SnCl₂, and zinc oxide, ZnO. The RIO composition is 30/70 resin/oil composition (here a paraffinic oil, Sunpar 150) the resin used is SP1045™ phenolic (octylphenol-formaldehyde resin with methylol active group). Detailed TPV formulations for masterbatches 5-1 to 5-16 are below in Table 6. Amounts are in grams. The adjustment ensures that the final and total oil amount in each formulation is the same. All TPVs were prepared in a Brabender internal mixer running at 180° C. (356° F.) and 100 RPM. PEDM masterbatch and PP were added at the beginning, after 1 minute, ½ of the oil was added, then after 2 min, the RIO was introduced, mixed for 1 min and SnCl₂/ZnO was added, mixed for another 5 min, finally the other ½ of oil was added and mixed for 3 minutes. The total mix time was 12 minutes. Data are reported in Tables 7A, 7B, 8A, and 8B.

TABLE 6 Recipe for Formulation One TPV's in Tables 7A, 7B, 8A, and 8B Formulation Formulation One One Ingredient Recipe One Recipe Two Polymers PEDM Master Batch (5-1 through 5-16) (g) 37.5 30.0 Plasticizer Sunpar ™ 150 (g) 12.50 15.00 iPP 5341 (g) 10.0 15.0 Curatives ROI (SP1045 ™ phenolic resin in oil 1.3 0.9 Sunpar ™ 150) (g) SnCl₂ (g) 0.2 0.1 ZnO (g) 0.5 0.4

TABLE 7A Particle size of TPV's-Formulation One Recipe One PEDM Area Particle PDI TPV Source coverage count Dn Dw Dv (Mw/Mn) Dv/Dn 7-1 3-1 0.56 10433 774.38 971.81 1151.29 1.25 1.49 7-2 3-2 0.52 9394 783.70 996.29 1182.38 1.27 1.51 7-3 3-3 0.60 3698 1381.44 1669.55 1897.22 1.21 1.37 7-4 3-4 0.52 9978 771.33 937.28 1082.00 1.22 1.40 7-5 3-5 0.57 10037 769.12 1023.74 1283.62 1.33 1.67 7-6 3-6 0.55 10132 786.23 969.53 1129.15 1.23 1.44 7-7 3-7 0.55 9915 781.69 991.80 1186.46 1.27 1.52 7-8 3-8 0.53 8739 807.61 1039.63 1269.90 1.29 1.57 7-9 3-9 0.52 9228 805.01 987.98 1143.25 1.23 1.42 7-10 3-10 0.49 9966 715.32 983.84 1214.14 1.38 1.70 7-11 3-11 0.51 8950 808.31 992.02 1150.49 1.23 1.42 7-12 3-12 0.51 8837 808.39 992.01 1152.49 1.23 1.43 7-13 3-13 0.51 8965 804.83 987.27 1144.39 1.23 1.42 7-14 3-14 0.50 8453 811.95 1022.10 1213.24 1.26 1.49 7-15 3-15 0.57 5087 1153.19 1385.12 1575.64 1.20 1.37 7-16 3-16 0.63 6748 1029.25 1269.68 1486.57 1.23 1.44

TABLE 7B Mechanical Properties of TPV's- Formulation One Recipe One Break Flex 2nd PEDM stress Strain mod 1st Hyst Hyst Shore A TPV Source (MPa) (%) (MPa) (J) (J) Hardness 7-1 3-1 6 290 22 0.87 0.42 68 7-2 3-2 6.72 356 21 0.70 0.31 67 7-3 3-3 5.56 291 35 0.95 0.60 69 7-4 3-4 5.56 318 22 0.83 0.44 67 7-5 3-5 7.59 325 24 1.05 0.60 69 7-6 3-6 7.39 363 21 1.03 0.60 68 7-7 3-7 4.81 226 20 0.87 0.49 67 7-8 3-8 7.88 363 25 1.03 0.59 71 7-9 3-9 7.04 379 20 0.97 0.56 68 7-10 3-10 6.99 344 22 1.03 0.57 66 7-11 3-11 6.47 344 19 0.82 0.47 66 7-12 3-12 7.34 358 20 0.84 0.48 67 7-13 3-13 7.07 349 19 0.87 0.51 65 7-14 3-14 8.04 360 20 1.09 0.63 67 7-15 3-15 5.59 286 34 0.89 0.57 68 7-16 3-16 6.14 282 38 0.93 0.59 69

TABLE 8A Particle size of TPV's-Formulation One Recipe Two PEDM Area Particle PDI TPV Source coverage count Dn Dw Dv (Mw/Mn) Dv/Dn 8-1 3-1 0.53 5863 811.3 1060.9 1292.1 1.31 1.59 8-2 3-2 0.57 6533 1005.2 1213.2 1394.2 1.21 1.39 8-3 3-3 0.53 5692 889.6 1325.8 1624 1.49 1.83 8-4 3-4 0.53 5863 1026.2 1234.5 1410 1.2 1.37 8-5 3-5 0.51 5808 984.1 1259.7 1462.1 1.28 1.49 8-6 3-6 0.53 10239 749.9 954.4 1153.8 1.27 1.54 8-7 3-7 0.53 10006 768.4 963.1 1147.2 1.25 1.49 8-8 3-8 0.58 8387 820.5 1170.8 1577.4 1.43 1.92 8-9 3-9 0.54 9872 764.9 985.8 1212.1 1.29 1.59 8-10 3-10 0.52 9708 763.9 980 1190.4 1.28 1.56 8-11 3-11 0.52 9568 770.1 979.8 1185.5 1.27 1.54 8-12 3-12 0.49 9374 769.4 951.6 1126.2 1.24 1.46 8-13 3-13 0.6 10580 771 1019.2 1300.6 1.32 1.69 8-14 3-14 0.47 8631 786.2 955.3 1099.1 1.22 1.4 8-15 3-15 0.54 6047 864.4 1461.9 1882.2 1.69 2.18 8-16 3-16 0.51 6904 811.1 1277.2 1613 1.58 1.99

TABLE 8B Mechanical Properties of TPV's-Formulation One Recipe Two PEDM Elongation Modulus 1st hyst 2nd hsyt Shore A TPV Source (%) (MPa) (J) (J) Hardness 8-1 3-1 323 41.3 1.03 0.41 78 8-2 3-2 410 43.2 1.1 0.52 77 8-3 3-3 385 57.2 1.17 0.62 80 8-4 3-4 419 43.4 1.18 0.57 78 8-5 3-5 375 41.9 1.1 0.49 78 8-6 3-6 354 43.4 1.1 0.5 77 8-7 3-7 406 39 1.09 0.52 75 8-8 3-8 418 44.7 1.18 0.52 78 8-9 3-9 501 42.1 1.13 0.55 77 8-10 3-10 379 38.1 1 0.46 76 8-11 3-11 493 38.2 1.09 0.54 76 8-12 3-12 409 37.4 1.08 0.53 77 8-13 3-13 486 39 1.14 0.56 77 8-14 3-14 439 40.9 1.1 0.53 78 8-15 3-15 486 57.2 1.12 0.59 77 8-16 3-16 392 62.5 1.28 0.62 81

Example 3 PEDM Synthesis for Formulation Two

PEDMs were produced using a solution process in a 0.5-liter continuous stirred-tank reactor (autoclave reactor). The autoclave reactor was equipped with a stirrer, a water-cooling/steam-heating element with a temperature controller, and a pressure controller.

Solvents and monomers were first purified by passing through a three-column purification system. The purification system consisted of an Oxiclear column (Model #RGP-R1-500 from Labclear) followed by a SA and a 3A molecular sieve column. Purification columns were regenerated periodically whenever there was evidence of low catalyst activity. Isohexane was used as a solvent. Solvent was fed into the reactor using a Pulsa pump and its flow rate was controlled by adjusting the outflow at the pump (using a calibration curve). The compressed, liquefied propylene feed was controlled by a mass flow controller. Ethylene was mixed with propylene before the reactor and fed to a reactant inlet manifold. A mixture of isohexane and tri-n-octylaluminum (TNOAL) and ethylene norbornene (ENB) was also added to the reactant inlet manifold through a separate line and the combined mixture of monomers and solvent was fed into the reactor using a single tube. Tri-n-octylaluminum (TNOAL, available from Sigma Aldrich, Milwaukee, Wis.) solution was diluted to a concentration of 1.843×10-6 using isohexane.

Isohexane and TNOAL solutions were fed using Pulsa pumps and their flow rate was controlled using a pump calibration curve. Purified propylene, and ENB were also fed using Pulsa pumps but their flow rate was controlled using mass-flow controllers. The feed rate of purified ethylene was also regulated using a mass flow controller. Ethylene and propylene combined into a single line before entering a manifold upstream of the reactor. Isohexane, TNOAL solution, and ENB solution lines also combined in a single line before entering the same manifold. The resulting two lines merged further downstream and the combined mixture of monomers and solvent was fed into the reactor using a single tube.

Catalyst used in these examples was dimethylsilylene(2,7,7-trimethyl-3,6,7,8-tetrahydro-as-indacen-3-yl)(t-butylamido)titanium dimethyl, and the activator used was dimethylaniliniumtetrakis(heptafluoronaphthyl)borate. Catalyst solution was prepared daily and used on the same day. The solution was prepared by dissolving 80 mg of the catalyst and 99.1 mg of the activator in 450 ml toluene (catalyst concentration=1.884×10-07 mol/ml, catalyst/activator (molar ratio)=0.98). This solution was pumped into the reactor through a designated dip-tube at a desired rate using an Isco pump.

Composition was controlled by adjusting the feed ratio of the monomers while the molecular weight of the polymer, under fixed feed conditions, was controlled using temperature. The collected samples were first placed on a boiling-water steam table in a hood to evaporate a large fraction of the solvent and unreacted monomers, and then, dried in a vacuum oven at a temperature of about 90° C. for about 12 hours. The vacuum oven dried samples were weighed to obtain yields. The ethylene and ENB content of the polymer was determined by FTIR. The monomer conversions were calculated using the polymer yield, composition and the amount of monomers fed into the reactor. Catalyst activity (also referred as to catalyst productivity) was calculated based the yield and the feed rate of catalyst. All the reactions were carried out at a gauge pressure of about 2.2 MPa. MST (Mooney Small Thin) measurements, MST and MSTRA (Mooney Small Thin Relaxation area,), were made as a proxy for molecular weight. Samples with ethylene concentration (FTIR-uncorrected) ranging from 16 wt % to 57.5 wt % and MST ranging from 17.5 to 61.5 were produced at a relatively fixed ENB concentration (2.7 to 3.4 wt %). Polymers were made according to the conditions described in Table 9A and the characterization data are reported in Table 10.

TABLE 9A PEDM Samples Cat Efficiency Mooney Sample Sample C2 ENB (g poly/g MST quantity Heat of ID (wt %) uncorrected (wt %) cat) (5 + 4) MSTRA (g) Fusion (J/g) 9-1 35.10% 5.60% 92490 79.11 1931 89.9 <0.25 9-2 33.80% 3.50% 99824 45.4 208 113.2 <0.25 9-3 32.80% 3.60% 84105 66 415 109 <0.25 9-4 31.90% 1.70% 92438 54.5 247 119.8 <0.25 9-5 32.10% 3.50% 76852 52.3 261 124.5 <0.25 9-6 33.10% 3.70% 57170 55.1 307 120.4 <0.25 9-7 14.20% 3.40% 113580 27.8  97 202.4 <0.25 9-8 14.70% 3.40% 126362 34.3 131 174 <0.25 9-9 15.80% 3.50% 110022 42.2 — 454.5 <0.25 9-10 22.60% 3.70% 118827 60.75 — 154 <0.25 9-11 21.80% 3.60% 110494 54.2 — 161.1 <0.25 9-12 35.00% 5.50% 46078 35.6 — 126.9 <0.25 9-13 34.50% 3.10% 63014 43 — 245 <0.25 9-14 22.80% 3.70% 122299 57.6 369 317 <0.25 9-15 55.50% 4.10% 85438 89.6 903 304.5 <0.25

TABLE 10 Characterization of PEDM Samples Sample Mw Mn Mz Mw/Mn ID (g/mol) (g/mol) (g/mol) (g/mol) 9-1 252870 107894 477125 2.34 9-2 753226 322661 1482937 2.33 9-3 552227 240021 1055490 2.30 9-4 609585 268969 1138523 2.27 9-5 558314 242187 1015968 2.31 9-6 550847 230979 1014947 2.38 9-7 512440 227138 930696 2.26 9-8 523470 233654 968590 2.24 9-9 628483 279375 1124578 2.25 9-10 690849 301194 1260055 2.29 9-11 660152 289470 1202015 2.28 9-12 421928 172729 819604 2.44 9-13 466408 201065 869371 2.32 9-14 695352 302513 1281416 2.30 9-15 581623 178942 1443793 3.25

The following samples: 9-9, 9-13, 9-14 and 9-15 were selected for further formation as TPV based their high molecular weight and the spread in the range of composition between the four polymers. The subsequent experiments were carried out with these four polymers. The PEDM's were combined with oil (either 75 or 100 phr) to make oil-extended PEDM's. These oil extended PEDM's were then converted into TPV's (Formulation Two-Recipe One or Two) according to the following general procedure: All TPVs were prepared in a Brabender internal mixer running at 180° C. (356° F.) and 100 RPM. EPDM, PEDM, and PP were added at the beginning, after 1 minute, ½ of the oil was added, then after 2 min, the RIO was introduced, mixed for 1 min and SnCl₂/ZnO was added, mixed for another 5 min, finally the other ½ of oil was added and mixed for 3 minutes. The total mix time was 12 minutes. Formulation Two recipes (in phr and grams) are reported in Table 11. The oil-extended PEDMs used in recipes One and Two are reported in Table 12. TPV's of selected oil extended PEDMs are reported in Tables 13, 14 and 14.

TABLE 11 Recipes for Formulation Two Formulation Formulation Formulation Formulation Two, Recipe Two, Recipe Two, Recipe Two, Recipe Sample One (phr) Two (phr) One (grams) Two (grams) Formula EPDM or PEDM 100 100 30.22 34.530.00 Oil incorporated in EPDM 75 100 4.66 4.66 PP5341 26.97 26.97 4.14 4.14 AMP 49974 (carbon black 23.96 23.96 7.25 7.25 masterbatch) Icecap K (Clay) 42 42.00 0.26 0.26 ZnO 1.5 1.50 2.26 0.0 Paramount 6001R (pre) 13.1 0.00 1.31 1.31 RIO-HRJ16261 (phenolic resin 7.56 7.56 0.29 0.29 in oil Paralux ™ 6001R) SnCl₂ masterbatch 1.67 1.67 9.62 7.57 Paramount ™ 6001R (post) 55.72 43.82 30.22 34.530.00

TABLE 12 Oil extension of PEDM for Formulation Two Recipe Recipe Recipe Recipe Recipe Recipe One One One One Two Recipe Two Two Sample 9-9A1 9-13A2 9-14A3 9-15A4 9-9B1 9-13B2 9-14B3 Formula (phr) 100.00 9-9 100.00 100.00 9-13 100.00 100.00 9-14 100.00 9-15 100.00 Paramount 6001R 75 75 75 75 100 100 100 (pre) Formula (grams) 9-9 34.29 0.00 0.00 0.00 30.00 0.00 0.00 9-13 0.00 34.29 0.00 0.00 0.00 30.00 0.00 9-14 0.00 0.00 34.29 0.00 0.00 0.00 30.00 9-15 0.00 0.00 0.00 34.29 Paramount 6001R 25.71 25.71 25.71 25.71 30.00 30.00 30.00 (pre) Total 60.00 60.00 60.00 60.00 60.00 60.00 60.00

TABLE 13 Example of inventive PEDM in combination with EPDM in Formulation Two, Recipe One Sample 7-101 7-102 7-103 7-107 7-108 7-109 Formula (grams) V3666 ™ EPDM 28.46 25.46 22.47 28.46 25.46 22.47 9-9A1 1.50 4.49 7.49 0.00 0.00 0.00 9-13A2 0.00 0.00 0.00 1.50 4.49 7.49 PP5341 ™ 4.46 4.46 4.46 4.46 4.46 4.46 AMP 4.10 4.10 4.10 4.10 4.10 4.10 49974 ™ (Carbon Black Masterbatch) IcecapK ™ (Clay) 7.19 7.19 7.19 7.19 7.19 7.19 ZnO 0.26 0.26 0.26 0.26 0.26 0.26 Paramount ™ 6001R 2.24 2.24 2.24 2.24 2.24 2.24 (pre) RIO HRJ16261 2.59 2.59 2.59 2.59 2.59 2.59 (Paralux 6001R) SnCl2 MB 0.57 0.57 0.57 0.57 0.57 0.57 Paramount 6001R 8.63 8.63 8.63 8.63 8.63 8.63 (post) Properties 25% Tension Set 6.00% 6.33% 7.50% 7.00% 6.17% 6.83% 50% Tension Set 13.00% 11.17% 14.33% 14.33% 13.17% 13.33% Morphology dn 648 681 688 563 606 580 dw 936 908 916 829 859 822 dz 1227 1096 1117 1128 1119 1091 dw/dn 1.44 1.33 1.33 1.47 1.42 1.42 dz/dw 1.31 1.21 1.22 1.36 1.30 1.33 Mechanicals DMTA Tensile (median) 4.74 5.1 5.1 4.99 4.71 4.66 % Strain (median) 259.79 278.95 246.84 256.62 254.55 275.25 Shore A Hardness 52.2 52.8 53.4 54 52.7 52.2 (median) Hysterisis Energy (first 0.45328 0.52793 0.63219 0.61869 0.59252 0.58559 deformation cycle) Median Energy (second 0.31666 0.36866 0.42953 0.41382 0.40853 0.39107 deformation cycle) Median

TABLE 14 Examples of PEDM with EPDM in Formulation Two, Recipe One (and comparatives in Recipe One and Two) 14D 14D 14D Comp. Recipe Recipe Recipe Comp. 1 2 one one one Recipe Recipe Example 7-113 7-114 7-115 One Two Formula (grams) 9-14 B3 1.50 4.49 7.49 PP5341 ™ 4.46 4.46 4.46 4.46 4.46 V3666 EPDM 28.46 25.46 22.47 29.96 0.00 w/75phr oil extension for comp 1 Keltan 597Q EPDM 0.000 34.24 w/ 100phr oil extension for comp 2 AMP 49974 ™ CB 4.10 4.10 4.10 4.10 4.10 IcecapK (Clay) 7.19 7.19 7.19 7.19 7.19 ZnO 0.26 0.26 0.26 0.26 0.26 Paramount 6001R 2.24 2.24 2.24 2.24 2.24 (pre) RIO HRJ16261 2.59 2.59 2.59 2.59 2.59 (Paralux 6001R) SnCl₂ MB 0.57 0.57 0.57 0.57 0.57 Paramount 6001R 8.63 8.63 8.63 8.63 6.60 (post) Properties 25% Tension Set 6.50% 5.83% 6.33% 7.50% 5.67% 50% Tension Set 13.00% 12.17% 12.25% 13.50% 10.75% Morphology dn 729 811 615 1234 1206 dw 1010 1059 912 1547 1582 dv 1221 1267 1239 1806 1979 dw/dn 1.39 1.31 1.48 1.25 1.31 dv/dw 1.21 1.20 1.36 1.17 1.25 Mechanicals DMTA Tensile (median) 5.04 4.94 5.22 4.26 3.87 % Strain (median) 262.84 230.95 292.22 233.55 194.92 Shore A Hardness 53.4 53.9 52.6 52.7 53.7 (median) Hysterisis Energy (first 0.58828 0.65202 0.61624 0.56475 0.582605 deformation cycle) Median Energy (second 0.40435 0.44365 0.42741 0.40372 0.421115 deformation cycle) Median

TABLE 15 Examples of inventive PEDM in combination with EPDM in Formulation Two, Recipe Two Sample 8-104 8-105 8-106 8-110 8-111 8-112 Formula (grams) Keltan ™ 5469Q 32.53 29.10 25.68 32.53 29.10 25.68 9-9B1 1.71 5.14 8.56 0.00 0.00 0.00 9-13B2 0.00 0.00 0.00 1.71 5.14 8.56 PP5341 ™ 4.46 4.46 4.46 4.46 4.46 4.46 AMP 49974 ™ (CB MB) 4.10 4.10 4.10 4.10 4.10 4.10 IcecapK ™ (Clay) 7.19 7.19 7.19 7.19 7.19 7.19 ZnO 0.26 0.26 0.26 0.26 0.26 0.26 RIO HRJ16261 (Paralux 2.59 2.59 2.59 2.59 2.59 2.59 6001R ™) SnCl2 MB 0.57 0.57 0.57 0.57 0.57 0.57 Paramount 6001R ™ 6.60 6.60 6.60 6.60 6.60 6.60 (post) Properties 25% Tension Set 6.25% 5.33% 5.50% 5.17% 6.00% 5.67% 50% Tension Set 11.50% 10.17% 10.17% 10.33% 10.50% 10.33% Morphology dn 653 618 619 675 647 593 dw 969 892 863 1000 879 900 dv 1323 1193 1097 1338 1094 1173 dw/dn 1.48 1.44 1.39 1.48 1.36 1.52 dv/dw 1.37 1.34 1.27 1.34 1.24 1.30 Mechanicals DMTA Tensile (median) 5.63 5.42 5.7 5.44 5.93 5.64 % Strain (median) 304.69 271.93 281.82 246.58 294.22 278.92 Shore A Hardness 54.6 54.3 54.7 54.6 53.6 53.8 (median) Hysterisis Energy (first 0.63297 0.67977 0.64344 0.69269 0.64544 0.64135 deformation cycle) Median Energy (second 0.43547 0.46955 0.43846 0.48277 0.44162 0.43593 deformation cycle) Median Sample 8-116 8-117 8-118 Formula (grams) Keltan ™5469Q 32.53 29.10 25.68 9-14B3 1.71 5.14 8.56 PP5341 ™ 4.46 4.46 4.46 AMP49974 ™ (CB MB) 4.10 4.10 4.10 IcecapK ™ (Clay) 7.19 7.19 7.19 ZnO 0.26 0.26 0.26 RIO HRJ16261 (Paralux 6001R) 2.59 2.59 2.59 SnCl2 MB 0.57 0.57 0.57 Paramount ™ 6001R (post) 6.60 6.60 6.60 Properties 25% Tension Set 5.67% 6.50% 5.00% 50% Tension Set 10.50% 10.17% 10.00% Morphology dn 632 626 620 dw 1006 865 946 dv 1469 1103 1307 dw/dn 1.59 1.38 1.52 dv/dw 1.46 1.27 1.38 Mechanicals DMTA Tensile (median) 5.9 6.43 4.25 % Strain (median) 299.04 330.7 196.46 Shore A Hardness (median) 54.8 54.9 55.1 Hysterisis Energy (first deformation cycle) Median 0.66398 0.67536 0.69541 Energy (second deformation cycle) Median 0.46176 0.46828 0.47462

While the present disclosure has been described and illustrated by reference to particular embodiments, those of ordinary skill in the art will appreciate that the disclosure lends itself to variations not necessarily illustrated herein. For this reason, then, reference should be made solely to the appended claims for purposes of determining the scope of the present disclosure. Further, the term “comprising” is considered synonymous with the term “including”. Likewise, whenever a composition, an element or a group of elements is preceded with the transitional phrase “comprising,” it is understood that we also contemplate the same composition or group of elements with transitional phrases “consisting essentially of,” “consisting of,” “selected from the group consisting of,” or “is” preceding the recitation of the composition, element, or elements and vice versa. 

What is claimed is:
 1. A thermoplastic vulcanizate comprising an isotactic polypropylene matrix phase in which a cross-linked ethylene-propylene-diene terpolymer (EPDM) is dispersed, the vulcanizate comprising the reaction product of: a) 35 to 55 wt % of an ethylene-propylene-diene terpolymer (EPDM); b) 10 to 40 wt % of isotactic polypropylene (iPP); c) 0.5 to 25 wt % of a propylene-ethylene-diene terpolymer (PEDM) compatibilizer, said compatibilizer having a heat of fusion of less than 2 J/g; and d) 0.015 to 0.03 wt % of curatives; wherein the percentages of components (a) to (d) are based on the total weight of the mixture.
 2. The thermoplastic vulcanizate of claim 1, further comprising at least 10 wt % of a diluent.
 3. The thermoplastic vulcanizate of claim 1, in which the EPDM comprises propylene, 55 to 75 wt % ethylene, and 2 to 10 wt % 5-ethylidene-2-norbornene.
 4. The thermoplastic vulcanizate of claim 1, in which amount of PEDM present is from 2 to 30 wt % of the amount of EPDM.
 5. The thermoplastic vulcanizate of claim 1, in which the PEDM has viscosity of MST (5+4) @230C is from 5 to
 90. 6. The thermoplastic vulcanizate of claim 1, in which the PEDM comprises 5 to 18 wt % ethylene and 2 to 12 wt % 5-ethylidene-2-norbornene.
 7. The thermoplastic vulcanizate of claim 1, wherein the particle size dispersity index (PSDI) of the rubber particles is less than
 3. 8. The thermoplastic vulcanizate of claim 1, further comprising clay and carbon black.
 9. The thermoplastic vulcanizate of claim 1, wherein the PEDM has a heat of fusion (Hf) which is less than 0.5 J/g.
 10. The thermoplastic vulcanizate of claim 1, wherein the PEDM has no detectable heat of fusion (Hf) when measured by DSC.
 11. A method for preparing a thermoplastic vulcanizate (TPV) comprising: i) mixing an iPP, EPDM, and PEDM having a heat of fusion of less than 2 J/g, and a diluent to prepare a TPV formulation; ii) adding one or more curatives to the TPV formulation and continuing mixing to perform dynamic vulcanization; and iii) recovering A TPV composition.
 12. The method of claim 11, further comprising adding a diluent to the TPV formulation prior to step ii) and continuing mixing.
 13. The method of claim 12, further comprising adding a further portion of diluent following step ii) and continuing mixing and dynamic vulcanization to form a TPV composition.
 14. The method of claim 13, in which the curatives are a phenolic resin in oil (RIO) composition, stannous chloride, and zinc oxide.
 15. The method of claim 14, in which the ethylene-propylene-diene terpolymer (EPDM) is added in an amount from 35-55 wt % of the TPV formulation, the isotactic polypropylene (iPP) is added in an amount from 10 to 40 wt % of the TPV formulation; diluent is added in an amount from 13 to 21 wt % of the TPV formulation, a propylene-ethylene-diene terpolymer (PEDM) compatibilizer is added in an amount from 0.5-15 wt % of the TPV formulation.
 16. The method of claim 15, which is performed at a temperature of from 150 to 200° C. in an internal mixer running at from 80 to 120 rpm and mixing continues for about 1 minute prior to step ii), for about 2 minutes after the first addition of diluent, for about 5 minutes after the second addition of diluent and for about 3 minutes after step iii).
 17. The method of claim 15, which is performed at a temperature from 200 to 250° C. in a continuous twin-screw extruder running at from 50 to 200 RPM with 1 to 5 minutes of residence time wherein the iPP, EPDM, and PEDM, and first portion of a diluent are added to the extruder at a first position of the extruder, and at least one of the second portion of diluent, the curatives and the third portion of diluent are added to the extruder at least a second position downstream from the first position.
 18. The method of claim 15, that is performed at a temperature of from 150 to 200° C. in an internal mixer running at from 80 to 120 rpm and mixing continues for about 1 minute after step i), for about 2 minutes after the first addition of diluent, for about 5 minutes after the second addition of diluent and for about 3 minutes after step iii); and then mixing is performed for about 1 to 5 additional minutes.
 19. The method of claim 15, that is performed at a temperature from 200 to 250° C. in a continuous twin-screw extruder running at from 50 to 200 RPM with 1 to 5 minutes of residence time; and in which the RIO composition is added to the extruder at a first position, followed by additional mixing.
 20. The method of claim 11, wherein the PEDM has a heat of fusion (Hf) which is greater than or equal to 0 and less than or equal to 2 J/g.
 21. The thermoplastic vulcanizate of claim 1, wherein the thermoplastic vulcanizate has a Dw/Dn of 7 or less.
 22. The thermoplastic vulcanizate of claim 1, wherein the thermoplastic vulcanizate has a tension set at 50% elongation of 14% or less.
 23. The thermoplastic vulcanizate of claim 1, wherein the thermoplastic vulcanizate has a tension set at 50% elongation of 14% or less and a Dw/Dn of 7 or less.
 24. The thermoplastic vulcanizate of claim 1, wherein the thermoplastic vulcanizate has: 1) a Dw/Dn of 7 or less; 2) a tension set at 50% elongation of 14% or less; 3) an elongation at break of 200% or more; 4) a break stress of 4 MPa or more; 5) a tension set from 25% elongation of 7% or less; 6) a number average particle size diameter of the rubber particles of 800 nm or less; 7) a dispersity of crosslinked particle size diameter of the rubber particles of 1.6 or less. 